Irradiation-Induced Microstructural Evolution and Mechanical Properties in Iron With and Without Helium

The results of the experiments and simulations were directly compared and related. The major findings included: (1) A link was established between the irradiated microstructure and its impact on mechanical properties. This was achieved through the quantitative evaluation of the ex-situ TEM defect analyses and the relationship of nanohardness to yield strength. The microstructural results from KMC modeling were also related to the mechanical properties through the Dispersed Barrier Model. (2) KMC was identified as a complementary technique for microstructural evaluation since it resulted in a distribution of defects that were not visible via TEM, however they are known to be present based on the PAS results. (3) PAS results and KMC simulations were compared with ATSUP calculations to quantify defect size versus positron lifetime.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Nuclear Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2015

Author dc:creator

• Okuniewski, Maria Ann

Contributors dc:contributor

• Stubbins, James F.

• Engineering, Materials Science

Language dc:language

eng

Identifier

(MiAaPQ)AAI3314862

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/85918