{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/85918"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/85918","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Irradiation-Induced Microstructural Evolution and Mechanical Properties in Iron With and Without Helium","abstract":"The results of the experiments and simulations were directly compared and related. The major findings included: (1) A link was established between the irradiated microstructure and its impact on mechanical properties. This was achieved through the quantitative evaluation of the ex-situ TEM defect analyses and the relationship of nanohardness to yield strength. The microstructural results from KMC modeling were also related to the mechanical properties through the Dispersed Barrier Model. (2) KMC was identified as a complementary technique for microstructural evaluation since it resulted in a distribution of defects that were not visible via TEM, however they are known to be present based on the PAS results. (3) PAS results and KMC simulations were compared with ATSUP calculations to quantify defect size versus positron lifetime.","abstract_html":"The results of the experiments and simulations were directly compared and related. The major findings included: (1) A link was established between the irradiated microstructure and its impact on mechanical properties. This was achieved through the quantitative evaluation of the ex-situ TEM defect analyses and the relationship of nanohardness to yield strength. The microstructural results from KMC modeling were also related to the mechanical properties through the Dispersed Barrier Model. (2) KMC was identified as a complementary technique for microstructural evaluation since it resulted in a distribution of defects that were not visible via TEM, however they are known to be present based on the PAS results. (3) PAS results and KMC simulations were compared with ATSUP calculations to quantify defect size versus positron lifetime.","abstract_has_math":false,"creators":["Okuniewski, Maria Ann"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Nuclear Engineering","degree_department":null,"school":null,"contributors":["Stubbins, James F."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2015,"date_issued":"2015-09-28T14:51:09Z","date_published":"2015-09-28T14:51:09Z","updated_at":"2026-07-22T22:26:26Z","subjects":["Engineering, Materials Science"],"languages":["eng"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(MiAaPQ)AAI3314862"],"render_values":[{"text":"(MiAaPQ)AAI3314862","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/85918","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Stubbins, James F."]},{"key":"dc:creator","label":"Author","values":["Okuniewski, Maria Ann"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2015-09-28T14:51:09Z","10000-01-01","2008"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Nuclear Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Materials Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/85918","(MiAaPQ)AAI3314862"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["The results of the experiments and simulations were directly compared and related. The major findings included: (1) A link was established between the irradiated microstructure and its impact on mechanical properties. This was achieved through the quantitative evaluation of the ex-situ TEM defect analyses and the relationship of nanohardness to yield strength. The microstructural results from KMC modeling were also related to the mechanical properties through the Dispersed Barrier Model. (2) KMC was identified as a complementary technique for microstructural evaluation since it resulted in a distribution of defects that were not visible via TEM, however they are known to be present based on the PAS results. (3) PAS results and KMC simulations were compared with ATSUP calculations to quantify defect size versus positron lifetime.","Made available in DSpace on 2015-09-28T14:51:09Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3314862.pdf: 5413255 bytes, checksum: fd6b016043c773d39e4190425eafd201 (MD5) Previous issue date: 2008","Embargo set by: Seth Robbins for item 87199 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","242 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2008."]},{"key":"dc:title","label":"Title","values":["Irradiation-Induced Microstructural Evolution and Mechanical Properties in Iron With and Without Helium"]}]}],"canonical_facts":{"dc:contributor":["Stubbins, James F."],"dc:creator":["Okuniewski, Maria Ann"],"dc:date":["2015-09-28T14:51:09Z","10000-01-01","2008"],"dc:description":["The results of the experiments and simulations were directly compared and related. The major findings included: (1) A link was established between the irradiated microstructure and its impact on mechanical properties. This was achieved through the quantitative evaluation of the ex-situ TEM defect analyses and the relationship of nanohardness to yield strength. The microstructural results from KMC modeling were also related to the mechanical properties through the Dispersed Barrier Model. (2) KMC was identified as a complementary technique for microstructural evaluation since it resulted in a distribution of defects that were not visible via TEM, however they are known to be present based on the PAS results. (3) PAS results and KMC simulations were compared with ATSUP calculations to quantify defect size versus positron lifetime.","Made available in DSpace on 2015-09-28T14:51:09Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3314862.pdf: 5413255 bytes, checksum: fd6b016043c773d39e4190425eafd201 (MD5) Previous issue date: 2008","Embargo set by: Seth Robbins for item 87199 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","242 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2008."],"dc:identifier":["http://hdl.handle.net/2142/85918","(MiAaPQ)AAI3314862"],"dc:language":["eng"],"dc:subject":["Engineering, Materials Science"],"dc:title":["Irradiation-Induced Microstructural Evolution and Mechanical Properties in Iron With and Without Helium"],"dc:type":["text"],"thesis:degree_discipline":["Nuclear Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:26Z"}