Core-Level Photoemission Investigations of the Cadmium-Telluride(100) and Indium-Antimony(100) Surface and Interfacial Structures

Photoemission techniques, utilizing a synchrotron light source, were used to analyze the clean (100) surfaces of the zinc-blende semiconductor materials CdTe and InSb. Several interfacial systems involving the surfaces of these materials were also studied, including the CdTe(100)-Ag interface, the CdTe(100)-Sb system, and the InSb(100)-Sn interface. High-energy electron diffraction was also employed to acquire information about of surface structure. A one-domain (2x1) structure was observed for the CdTe(100) surface. Analysis of photoemission spectra of the Cd 4d core level for this surface structure revealed two components resulting from Cd surface atoms. The total intensity of these components accounts for a full monolayer of Cd atoms on the surface. A structural model is discussed commensurate with these results. Photoemission spectra of the Cd and Te 4d core levels indicate that Ag or Sb deposited on the CdTe(100)-(2x1) surface at room temperature do not bound strongly to the surface Cd atoms. The room temperature growth characteristics for these two elements on the CdTe(100)-(2x1) are discussed. The growth at elevated substrate temperatures was also studied for Sb deposition. The InSb(100) surface differed from the CdTe(100) surface. Using molecular beam epitaxy, several structures could be generated for the InSb(100) surface, including a c(8x2), a c(4x4), an asymmetric (1x3), a symmetric (1x3), and a (1x1). Analysis of photoemission intensities and line shapes indicates that the c(4x4) surface is terminated with 1${3\over 4}$ monolayers of Sb atoms. The c(8x2) surface is found to be terminated with ${3\over 4}$ monolayer of In atoms. Structural models for both of these surfaces are proposed based upon the photoemission results and upon models of the similar GaAs(100) structures. The room temperature growth characteristics of grey Sn on the InSb(100)-c(4x4) and InSb(100)-c(8x2) surfaces were studied with photoemission. The discontinuity in the valence band maximum for this semiconductor heterojunction system is measured to be 0.40 eV, independent of the starting surface structure and stoichiometry. This result is reconciled with theoretical predictions for heterostructure behavior.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Physics

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2015

Author dc:creator

• John, Peter James

• Physics, Condensed Matter

Language dc:language

eng

Identifier

(UMI)AAI8908720

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/77427