Role of surface chemistry in sub-Einstein rheology of nano-composites

Sub-Einstein and negative intrinsic viscosities resulting from the addition of nano-fillers to polymer melts approximately 2-10 nm diameter have been reported. Here we explore the intrinsic viscosity of polyhedral oligomeric silisequioxane (POSS) particles of approximately 1.6-2.5 nm diameters as a function of polymer molecular weight. These nanoparticles consist of cubes of 8-corner silicon atoms edge bridged with oxygen atoms. A variety of functional groups are attached to the corner silicon atoms. Three different POSS particles are explored: POSS with 8 tethered alkyl chains (butyl and octyl) and POSS with 8 tethered polyethylene glycol, PEG, chains of degree of polymerization, n ~ 13 segments. The tethered particles are dissolved in a homopolymer matrix (polydimethyl siloxane, PDMS, for octyl-POSS and butyl-POSS and PEG for PEG-POSS). The POSS intrinsic viscosity drops with increasing polymer matrix molecular weight from approximately 2.5 (as predicted by Einstein for no slip boundary conditions) to negative values. We discuss these results in light of previous studies of the intrinsic viscosity of nanoparticles in polymer melts with special attention to particle-polymer segment surface interactions that result in particle-polymer miscibility and ideas based on the ability of nanoparticles to alter polymer relaxation rates. We develop a hypothesis that negative intrinsic viscosities are associated with weak particle-polymer segment surface interactions while at the same time developing mechanisms that ensure particles remain soluble in the polymer melt.

Name thesis:degree_name

M.S.

Level thesis:degree_level

Thesis

Discipline thesis:degree_discipline

Chemical Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2012

Author dc:creator

• Ranka, Moulik

Contributors dc:contributor

• Zukoski, Charles F.

• polyhedral oligomeric silisequioxane (POSS)
• Rheology
• Nano-Composite
• Intrinsic Viscosity

Statement dc:rights

• Copyright 2012 Moulik Ranka

Language dc:language

en

Handle dc:identifier

http://hdl.handle.net/2142/34404

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/34404