{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/34404"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/34404","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Role of surface chemistry in sub-Einstein rheology of nano-composites","abstract":"Sub-Einstein and negative intrinsic viscosities resulting from the addition of nano-fillers to polymer melts approximately 2-10 nm diameter have been reported. Here we explore the intrinsic viscosity of polyhedral oligomeric silisequioxane (POSS) particles of approximately 1.6-2.5 nm diameters as a function of polymer molecular weight. These nanoparticles consist of cubes of 8-corner silicon atoms edge bridged with oxygen atoms. A variety of functional groups are attached to the corner silicon atoms. Three different POSS particles are explored: POSS with 8 tethered alkyl chains (butyl and octyl) and POSS with 8 tethered polyethylene glycol, PEG, chains of degree of polymerization, n ~ 13 segments. The tethered particles are dissolved in a homopolymer matrix (polydimethyl siloxane, PDMS, for octyl-POSS and butyl-POSS and PEG for PEG-POSS). The POSS intrinsic viscosity drops with increasing polymer matrix molecular weight from approximately 2.5 (as predicted by Einstein for no slip boundary conditions) to negative values. We discuss these results in light of previous studies of the intrinsic viscosity of nanoparticles in polymer melts with special attention to particle-polymer segment surface interactions that result in particle-polymer miscibility and ideas based on the ability of nanoparticles to alter polymer relaxation rates. We develop a hypothesis that negative intrinsic viscosities are associated with weak particle-polymer segment surface interactions while at the same time developing mechanisms that ensure particles remain soluble in the polymer melt.","abstract_html":"Sub-Einstein and negative intrinsic viscosities resulting from the addition of nano-fillers to polymer melts approximately 2-10 nm diameter have been reported. Here we explore the intrinsic viscosity of polyhedral oligomeric silisequioxane (POSS) particles of approximately 1.6-2.5 nm diameters as a function of polymer molecular weight. These nanoparticles consist of cubes of 8-corner silicon atoms edge bridged with oxygen atoms. A variety of functional groups are attached to the corner silicon atoms. Three different POSS particles are explored: POSS with 8 tethered alkyl chains (butyl and octyl) and POSS with 8 tethered polyethylene glycol, PEG, chains of degree of polymerization, n ~ 13 segments. The tethered particles are dissolved in a homopolymer matrix (polydimethyl siloxane, PDMS, for octyl-POSS and butyl-POSS and PEG for PEG-POSS). The POSS intrinsic viscosity drops with increasing polymer matrix molecular weight from approximately 2.5 (as predicted by Einstein for no slip boundary conditions) to negative values. We discuss these results in light of previous studies of the intrinsic viscosity of nanoparticles in polymer melts with special attention to particle-polymer segment surface interactions that result in particle-polymer miscibility and ideas based on the ability of nanoparticles to alter polymer relaxation rates. We develop a hypothesis that negative intrinsic viscosities are associated with weak particle-polymer segment surface interactions while at the same time developing mechanisms that ensure particles remain soluble in the polymer melt.","abstract_has_math":false,"creators":["Ranka, Moulik"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"M.S.","degree_level":"Thesis","degree_discipline":"Chemical Engineering","degree_department":null,"school":null,"contributors":["Zukoski, Charles F."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2012,"date_issued":"2012-09-18T21:15:17Z","date_published":"2012-09-18T21:15:17Z","updated_at":"2026-07-22T22:25:31Z","subjects":["polyhedral oligomeric silisequioxane (POSS)","Rheology","Nano-Composite","Intrinsic Viscosity"],"languages":["en"],"rights":["Copyright 2012 Moulik Ranka"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/34404","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Zukoski, Charles F."]},{"key":"dc:creator","label":"Author","values":["Ranka, Moulik"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2012-09-18T21:15:17Z","2012-08"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Chemical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["polyhedral oligomeric silisequioxane (POSS)","Rheology","Nano-Composite","Intrinsic Viscosity"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 2012 Moulik Ranka"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/34404"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Sub-Einstein and negative intrinsic viscosities resulting from the addition of nano-fillers to polymer melts approximately 2-10 nm diameter have been reported. Here we explore the intrinsic viscosity of polyhedral oligomeric silisequioxane (POSS) particles of approximately 1.6-2.5 nm diameters as a function of polymer molecular weight. These nanoparticles consist of cubes of 8-corner silicon atoms edge bridged with oxygen atoms. A variety of functional groups are attached to the corner silicon atoms. Three different POSS particles are explored: POSS with 8 tethered alkyl chains (butyl and octyl) and POSS with 8 tethered polyethylene glycol, PEG, chains of degree of polymerization, n ~ 13 segments. The tethered particles are dissolved in a homopolymer matrix (polydimethyl siloxane, PDMS, for octyl-POSS and butyl-POSS and PEG for PEG-POSS). The POSS intrinsic viscosity drops with increasing polymer matrix molecular weight from approximately 2.5 (as predicted by Einstein for no slip boundary conditions) to negative values. We discuss these results in light of previous studies of the intrinsic viscosity of nanoparticles in polymer melts with special attention to particle-polymer segment surface interactions that result in particle-polymer miscibility and ideas based on the ability of nanoparticles to alter polymer relaxation rates. We develop a hypothesis that negative intrinsic viscosities are associated with weak particle-polymer segment surface interactions while at the same time developing mechanisms that ensure particles remain soluble in the polymer melt.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2012-07-16T13:44:02Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 1 Ranka_Mouik.pdf: 949541 bytes, checksum: 71661580f172aa040a6cb2d3ecc44e2a (MD5)","Made available in DSpace on 2012-09-18T21:15:17Z (GMT). No. of bitstreams: 2 Ranka_Moulik.pdf: 949466 bytes, checksum: b4984c2df7d6684a6da69987328a2ca0 (MD5) license.txt: 4060 bytes, checksum: 563b969590fb9088288eb4a6d96fde4f (MD5)"]},{"key":"dc:title","label":"Title","values":["Role of surface chemistry in sub-Einstein rheology of nano-composites"]}]}],"canonical_facts":{"dc:contributor":["Zukoski, Charles F."],"dc:creator":["Ranka, Moulik"],"dc:date":["2012-09-18T21:15:17Z","2012-08"],"dc:description":["Sub-Einstein and negative intrinsic viscosities resulting from the addition of nano-fillers to polymer melts approximately 2-10 nm diameter have been reported. Here we explore the intrinsic viscosity of polyhedral oligomeric silisequioxane (POSS) particles of approximately 1.6-2.5 nm diameters as a function of polymer molecular weight. These nanoparticles consist of cubes of 8-corner silicon atoms edge bridged with oxygen atoms. A variety of functional groups are attached to the corner silicon atoms. Three different POSS particles are explored: POSS with 8 tethered alkyl chains (butyl and octyl) and POSS with 8 tethered polyethylene glycol, PEG, chains of degree of polymerization, n ~ 13 segments. The tethered particles are dissolved in a homopolymer matrix (polydimethyl siloxane, PDMS, for octyl-POSS and butyl-POSS and PEG for PEG-POSS). The POSS intrinsic viscosity drops with increasing polymer matrix molecular weight from approximately 2.5 (as predicted by Einstein for no slip boundary conditions) to negative values. We discuss these results in light of previous studies of the intrinsic viscosity of nanoparticles in polymer melts with special attention to particle-polymer segment surface interactions that result in particle-polymer miscibility and ideas based on the ability of nanoparticles to alter polymer relaxation rates. We develop a hypothesis that negative intrinsic viscosities are associated with weak particle-polymer segment surface interactions while at the same time developing mechanisms that ensure particles remain soluble in the polymer melt.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2012-07-16T13:44:02Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 1 Ranka_Mouik.pdf: 949541 bytes, checksum: 71661580f172aa040a6cb2d3ecc44e2a (MD5)","Made available in DSpace on 2012-09-18T21:15:17Z (GMT). No. of bitstreams: 2 Ranka_Moulik.pdf: 949466 bytes, checksum: b4984c2df7d6684a6da69987328a2ca0 (MD5) license.txt: 4060 bytes, checksum: 563b969590fb9088288eb4a6d96fde4f (MD5)"],"dc:identifier":["http://hdl.handle.net/2142/34404"],"dc:language":["en"],"dc:rights":["Copyright 2012 Moulik Ranka"],"dc:subject":["polyhedral oligomeric silisequioxane (POSS)","Rheology","Nano-Composite","Intrinsic Viscosity"],"dc:title":["Role of surface chemistry in sub-Einstein rheology of nano-composites"],"thesis:degree_discipline":["Chemical Engineering"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["M.S."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:31Z"}