Antimony-based type-II superlattice infrared photodetectors on indium-arsenide substrates

The wide variety of applications for mid- and far-infrared detection has spurred the study of cutting-edge technologies for use in the next genera- tion of detectors in place of the current systems, such as mercury cadmium telluride. While type-II superlattices over a number of advantages in design and material quality, theoretical predictions of their high performance have yet to be realized. This work concentrates on novel designs, fabrication, and characterization of type-II superlattice infrared detectors. In this work we present the first InAs/GaSb type-II superlattice photode- tectors grown on an InAs substrate via metal-organic chemical vapor depo- sition. The design and fabrication of the devices are detailed, along with several characterization processes, including low-temperature electron beam induced current (EBIC) to study structural defects. Through this work, the optical absorption of the undoped substrate was shown to be significantly lower than that of GaSb. The detectors have a cutoff wavelength (50% re- sponsivity) of 9.5 um at 78 K. Their R0A values are on the order of 10^-2 Ohm*cm2. The typical peak responsivity is 1.9 A/W, and the devices have a peak detectivity of 6.8 * 10^9 cm*Hz^1/2 /W at 78 K.

Name thesis:degree_name

M.S.

Level thesis:degree_level

Thesis

Discipline thesis:degree_discipline

Electrical & Computer Engr

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2011

Author dc:creator

• Zuo, Daniel Y.

Contributors dc:contributor

• Chuang, Shun-Lien

• Infrared detectors
• Type-II Superlattice
• Photodiode
• InAs substrate
• electron beam induced current (EBIC)

Statement dc:rights

• Copyright 2011 Daniel Y. Zuo

Language dc:language

en

Handle dc:identifier

http://hdl.handle.net/2142/26349

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/26349