Novel Poly(N-substituted glycine)s : synthesis, post-modification, and physical properties

Various synthetic approaches were explored towards the preparation of poly(N-substituted glycine) homo/co-polymers (a.k.a. polypeptoids). In particular, monomers that would facilitate in the preparation of bio-relevant polymers via either chain- or step-growth polymerization were targeted. A 3-step synthetic approach towards N-substituted glycine N-carboxyanhydrides (NNCA) was implemented, or developed, and optimized allowing for an efficient gram scale preparation of the aforementioned monomer (chain-growth). After exploring several solvents and various conditions, a reproducible and efficient ring-opening polymerization (ROP) of NNCAs was developed in benzonitrile (PhCN). However, achieving molecular weights greater than 7 kDa required longer reaction times (>4 weeks) and sub-sequentially allowed for undesirable competing side reactions to occur (eg. zwitterion monomer mechanisms). A bulk-polymerization strategy provided molecular weights up to 11 kDa within 24 hours but suffered from low monomer conversions (ca. 25%). Likewise, a preliminary study towards alcohol promoted ROP of NNCAs suffered from impurities and a suspected alternative activated monomer mechanism (AAMM) providing poor inclusion of the initiator and leading to multi-modal dispersed polymeric systems. The post-modification of poly(N-allyl glycine) via thiol-ene photo-addition was observed to be quantitative, with the utilization of photo-initiators, and facilitated in the first glyco-peptoid prepared under environmentally benign conditions. Furthermore, poly(N-allyl glycine) demonstrated thermo-responsive behavior and could be prepared as a semi-crystalline bio-relevant polymer from solution (ie. annealing). Initial efforts in preparing these polymers via standard poly-condensation protocols were insufficient (step-growth). However, a thermally induced side-product, diallyl diketopiperazine (DKP), afforded the opportunity to explore photo-induced thiol-ene and acyclic diene metathesis (ADMET) polymerizations. Thiol-ene polymerization readily led to low molecular weight polymers (<2.5 kDa), that were insoluble in most solvents except heated amide solvents (ie. DMF), whereas ADMET polymerization, with diallyl DKP, was unsuccessful due to a suspected 6 member complexation/deactivation state of the catalyst. This understanding prompted the preparation of elongated DKPs most notably dibutenyl DKP. SEC data supports the aforementioned understanding but requires further optimization studies in both the preparation of the DKP monomers and following ADMET polymerization. This work was supported by NMR, GC-MS, FT-IR, SEC-IR, and MALDI-Tof MS characterization. Polymer properties were measured by UV-Vis, TGA, and DSC.

Level thesis:degree_level

thesis.doctoral

Grantor dc:publisher

Universität Potsdam

Year

2013

Author dc:creator

• Robinson, Joshua Wayne

Contributors dc:contributor

• Schlaad, Helmut

• Glycopeptoid
• Polyglycin
• NCA
• biorelevant
• thermoresponsiv
• polyglycine
• thermoresponsive

Statement dc:rights

• Creative Commons - Namensnennung, Weitergabe zu gleichen Bedingungen 3.0 Deutschland

Repository record source_url

https://publishup.uni-potsdam.de/frontdoor/index/index/docId/6245

OAI identifier oai:identifier

oai:kobv.de-opus4-uni-potsdam:6245