Intraoral Corrosion of Self-ligating Metallic Brackets and Archwires and the Effect on Friction

The purpose of this study was to investigate how the frictional coefficient was affected due to intraoral use. A secondary aim of this study was to determine whether or not there was a relationship between corrosion of orthodontic alloys and friction via scanning electron microscopic qualitative analysis. Orthodontic brackets and 0.019 x 0.025 inch stainless steel archwires were collected and divided into three groups of n=10: used bracket and used wires (UBUW), used brackets and new wires (UBNW), and new brackets and new wires (NBNW). ‘New’ materials were as-received from the manufacturer, and ‘used’ materials were clinically used bracket and wires collected from patients following orthodontic treatment. Archwires were pulled through bracket slots at a rate of 0.5mm/min while friction forces were measured. Following a cleaning process, the surface topography of the bracket slots was examined under a scanning electron microscope (SEM). Based on a 1-factor MANOVA, there was no significant group effect (all p>0.05) on frictional forces. Partial eta squared values indicated that intraoral exposure had only a small effect on frictional forces (≤ 3%). Qualitative analysis of SEM images did not show an association between surface characteristics of the bracket slots and magnitude of frictional force. Results suggest that surface corrosion from intraoral use does not significantly affect friction at the bracket wire interface.

Name thesis:degree_name

M.S.

Level thesis:degree_level

Masters

Discipline thesis:degree_discipline

Oral and Craniofacial Sciences (UMKC)

Grantor

University of Missouri--Kansas City

Year dc:date.issued

2014

Author dc:creator

• Tima, Lori Lynn

Advisor dc:contributor.advisor

• Nickel, Jeffrey C. (Jeffrey Charles), 1957-

Handle dc:identifier.uri

https://hdl.handle.net/10355/45633

OAI identifier oai:identifier

oai:mospace.umsystem.edu:10355/45633