Estimation of Adhesive Bond Strength in Laminated Safety Glass Using Guided Mechanical Waves

Based upon the guided wave energy velocity predictions for each of the laminates with different levels of adhesion, the S0 mode was selected as the most promising for use in nondestructively estimating adhesion levels in laminated safety glass. The predicted energy velocities (obtained using this multilayered model) were validated using guided wave energy velocity experimental measurements. The experimentally obtained velocity measurements are in good agreement with the predicted values. Guided wave attenuation in laminated safety glass is primarily due to the viscoelastic material properties of the PVB plastic interlayer. The attenuation properties of S1 mode were also explored to estimate the adhesive bond strength between the plastic interlayer and the two adjacent glass plates. Results show that the combination of both the energy velocity and attenuation methods has promise towards replacing the pummel test method to estimate the adhesion level in laminated safety glass.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Systems and Entrepreneurial Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2015

Author dc:creator

• Huo, Shihong

Contributors dc:contributor

• Henrique Reis

• Engineering, Aerospace

Language dc:language

eng

Identifier

(MiAaPQ)AAI3314798

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/87086