Molecular Dynamics Study of Microstructural Evolution in Alloys Subjected to Severe Plastic Deformation

The atomic transport resulting from plastic deformation has been analyzed in new depths by tracking the evolution of pair of marker atoms. This analysis has proved to be a powerful tool in identifying the deformation mechanisms, including the glide of leading and trailing partial dislocations, and vacancy assisted atomic jumps during deformation, as well as quantifying the relative contributions of these mechanisms. It is found that the glide of dislocations plays a more important role than previously thought in accommodating plastic deformation in nanocrystalline alloys. A new property of the atomic mixing by plastic deformation that has been uncovered is that the effective diffusion coefficient increases, nearly linearly, with the separation distance of pairs of atoms. This superdiffusive mixing is revealed by monitoring the relative displacement of atoms as a function of the separation distance. This result can be tested experimentally by measuring the rate of dissolution of precipitates during deformation. This finding also provides a direct rationalization for the stabilization of compositional patterns when thermal diffusion and forced mixing compete.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Materials Science and Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2015

Author dc:creator

• Odunuga, Samson Olusikunanu

Contributors dc:contributor

• Averback, Robert S.

• Engineering, Metallurgy