Design of Improved Ceramic/polymeric Composites

The last chapter deals with the design, fabrication, and evaluation of a new coupling agent for glass fiber/epoxy matrix composites. This interface consisted of a thin coating of activated carbon (ACI) with high surface area to take advantage of mechanical interlocking. Furthermore, the surface chemistry was modified to provide varying degrees of bonding to the resin. These ACI provided equivalent moduli when compared to similar composites using commercial coupling agents. Hygrothermal aging showed the basic surface chemistry ACI to be extremely resistant to mechanical property degradation. The ACI systems displayed two distinct failure modes, fiber/matrix fracture and fiber debonding, controlled by the interface strength and thus the surface chemistry. These different failure modes led to a damage evolution study via thermoelastic stress analysis.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Materials Science and Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2015

Author dc:creator

• Seghi, Steven Monte

Contributors dc:contributor

• Economy, James

• Engineering, Materials Science

Language dc:language

eng

Identifier

(MiAaPQ)AAI3101965

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/82745