{112} Polar Surfaces of Copper(indium,gallium)selenide: Properties and Effects on Crystal Growth

Cu(In,Ga)Se2 (GIGS) are promising materials for thin film photovoltaic applications. This work studies the epitaxial growth of CIGS single crystal films on GaAs substrates of various orientations and characterizes the properties of the thin films. A surprising finding is the strong tendency of film surfaces to facet to {112} planes. The work attempted to establish the connections between the film morphology, the surface energies, the surface chemical compositions, and the reconstruction of polar surfaces. Using angle-resolved photoelectron emission spectroscopy, I found that there is a severe Cu depletion at the first 1--2 layer of the free surface of CuInSe2 and the surface is semiconducting. The results strongly support the model of a reconstructed non-stoichiometric polar surface and exclude the previously believed existence of a bulk second phase on the CIS surface. Unique features of the film morphology suggest that the properties and structure of the polar surfaces have great effects on the growth of the crystals, and probably on the incorporation of the large amount of point defects. Measured chemical composition profiles indicate that the Cu depletion observed on free CIGS surface remains at the CIGS/CdS heterojunction interface and Cd is incorporated into the surface of CIGS. It is proposed that this non-stoichiometric composition leads to charge imbalance at the interface and causes the type-inversion of the CIGS surface, which are favorable for the device performance.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Materials Science and Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2003

Author dc:creator

• Liao, Dongxiang

Contributors dc:contributor

• Rockett, Angus A.

• Engineering, Materials Science

Language dc:language

eng

Identifier

(MiAaPQ)AAI3101902

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/82742