Investigation of defects on acoustic scattering in cloak by molding process

For this paper, molding- and casting-based microfabrication of metal microstructures was developed in order to replicate the acoustic cloak. The metal was cast into a stretchable PDMS mold, which was cast from micromachined aluminum cloak. For the PDMS mold, the mold release agent, trichlorosilane ([tridecafluoro-1,1,2,2-tetrahydrooctyl] trichlorosilane), was enhanced to imprint the micro-sized features of aluminum cloak in a circular area with a diameter of 105mm. This micromold process with trichlorosilane was also demonstrated by casting silicone rubber into original acoustic cloak. The low-temperature metal alloy, CerroBend, was used to microcast the metamaterial networks at a melting point of 70°C. Some damaged replicas were prepared to investigate defects in the cloak, and the performance of the broken cloak was estimated by the acoustic measurement in the water at an operating frequency of 60 kHz. We demonstrated that the broken cloak could accomplish the cloaking function depending on the direction of defects. Moreover, this study of microcasting process for the mass production and investigation of the defects in the acoustic cloak may apply to the understanding of the broken symmetric effects of an acoustic metamaterial.

Name thesis:degree_name

M.S.

Level thesis:degree_level

Thesis

Discipline thesis:degree_discipline

Mechanical Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2012

Author dc:creator

• Cho, Shinhu

Contributors dc:contributor

• Fang, Nicholas X.

• Acoustic Metamaterial
• Micro-molding
• Micro-casting
• Scattering effect

Statement dc:rights

• Copyright 2011 Shinhu Cho

Language dc:language

en

Handle dc:identifier

http://hdl.handle.net/2142/29807

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/29807