Complex oxides of the system Cu-Ni-Fe-O: synthesis parameters, phase formation and properties
Abstract
dc:description.abstractThis thesis describes the convenient routes and the preparation conditions (temperature, oxygen partial presssure) which lead to the formation of single phase materials within the quaternary system Cu-Ni-Fe-O. The investigated compositions are the solid solutions CuxNi1-xFe2O4, the ferrites occurring in the phase triangle Cu0.5Ni0.5Fe2O4 -Cu0.9Fe2.1O4 - Cu0.5Fe2.5O4 and some copper-nickel oxide solid solutions. Three synthesis routes have been used, namely (i) the preparation and the thermal decomposition of freeze-dried carboxylate precursors, (ii) the preparation and the oxidation of intermetallic phases and (iii) the preparation and the heat treatment in air of mixed oxide/metallic powders. The thermal decomposition of freeze-dried Cu-Ni-Fe formate has been found as a suitable method for preparing single spinel phases within the Cu-Ni-Fe-O system. In comparison with the conventional solid state reaction, the required temperature is much lower. Concerning the solid solution CuxNi1-xFe2O4 , a single phase spinel is formed at 1000¢XC for x < 0.7; for CuO is identified as second phase. In this latter range the formation of a pure phase required an increase of the iron content in the mixture. The other single spinel phases in the phase triangle Cu0.5Ni0.5Fe2O4 - Cu0.9Fe2.1O4 - Cu0.5Fe2.5O4 have been synthesized under special synthesis p(O2)/T-conditions. For copper ferrites Cu1-xFe2+xO4 with x ? 0.1, 0.2, 0.33, 0.4 and 0.5, the change in the conductivity with the temperature is irreversible. The deviation from the linearity of the conductivity ?ã as a function of the temperature occurs due to the thermal history of these samples. The saturation magnetic moment (nB) at 5K, of some synthesized CuxNi1-xFe2O4 compounds has been determined. It has been found that nB increases with the nickel content in the ferrite sample.
Degree
thesis:*- Level thesis:degree_level
- thesis.doctoral
- Grantor dc:publisher
- Technische Universität Dresden
- Year
- 2004
Author and committee
dc:creator, dc:contributor.*- Author dc:creator
-
- Kenfack, Flaurance
- Contributors dc:contributor
-
- Langbein, Hubert
- Ullmann, Helmut
- Roewer, Gerhard