Dynamic actuation properties of Ni-Mn-Ga ferromagnetic shape memory alloys

Dynamic magnetic-field-induced strain actuation of up to 3% with a frequency bandwidth of least 500 Hz in Ni48.5Mn29.5Ga21 ferromagnetic shape memory alloys (FMSAs) is achieved. Hardware was designed and constructed to measure frequency bandwidth, magnetic-field-induced strain, stress and magnetization driven from an applied magnetic field. The bandwidth in this investigation was only limited by inductive reactance of the hardware, not by fundamental limitations of Ni-Mn-Ga. Degradation of the peak dynamic actuation strain occurred from 3.0% to 2.6% with increasing number of cycles from Nz1,000 to N 100,000. Measurement of strain, stress, and magnetization driven by a magnetic field permitted the comparison of measured properties versus properly defined thermodynamic properties. The peak thermodynamic piezomagnetic coefficient is d3, 1,= 2.5 x 10-7m / A compared to the experimental slope, dE/dH, of 1.0 x 10-7 m / A at N-1,000 cycles and 1.4 x 10-7 m / A at N-100,000 cycles, respectively. The thermodynamic piezomagnetic coefficient is five times greater than Terfenol-D with d31 = 5.0 x 10-m / A. The magnetic susceptibility varies between 3-10, while the twinning stiffness varies between 30-40 MPa within the average bias stress range of 0.3 to 2.8 MPa. At optimum fields and bias stresses, the mechanical energy density during cyclic deformation was 65 kJ/m3 at the expense of 20 kJ/m3 lost An important first observation of dynamic stress vs. field behavior is understood by an extension of a magnetomechanical phenomenological model.

Department dc:contributor.department

Massachusetts Institute of Technology. Department of Materials Science and Engineering

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2002

Author dc:creator

• Henry, Christopher P. (Christopher Paul), 1974-

Advisor dc:contributor.advisor

• Samuel M. Allen and Robert C. O'Handley.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/8442

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/8442