Paint-bake effect on the plasticity and fracture of pre-strained aluminum 6451 sheets

In automotive engineering, sheet metal components are subject to a 20 min heat treatment at 180°C during paint baking. This process may significantly alter the mechanical properties of 6000-series aluminum alloys through artificial ageing. Here, a comprehensive experimental program is carried out to characterize the anisotropic plasticity and the fracture initiation in prestrained artificially-aged aluminum 6451 sheets. It is found that the combination of pre-straining up to 5% strain and heat treatment mainly changes the material's strain hardening behavior and the stress-state sensitivity of its fracture response. The material parameters of the Yld2000-2d plasticity model with combined Swift-Voce hardening are identified for four distinct materials from uniaxial tension and shear experiments. The corresponding Hosford-Coulomb fracture model parameters are determined from smiley shear, V-bending and punch experiments. As an important byproduct of the research, the Yld2000-2d and Hosford-Coulomb models are successfully validated for all four materials through notched and central hole tension experiments. Simple empirical expressions are also provided to estimate the material properties as a function of the prestrain in engineering practice.

Department dc:contributor.department

Massachusetts Institute of Technology. Department of Mechanical Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2017

Author dc:creator

• Abi Akl, Rami

Advisor dc:contributor.advisor

• Tomasz Wierzbicki.

• Mechanical Engineering.

Statement dc:rights

• MIT theses are protected by copyright. They may be viewed, downloaded, or printed from this source but further reproduction or distribution in any format is prohibited without written permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/108903

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/108903