Polyurethane foams containing renewable castor oil replacement

Polyurethane foams have a wide variety of commercial applications in daily life due to their unique advantages. Traditionally, polyurethane foams are made from petroleum-based polyols and isocyanates. Due to the shortage of fossil resources, renewable biobased materials are studied as alternatives to petroleum. In this project, castor oil was chosen as a renewable biobased polyol in order to replace the nonrenewable petroleum-based polyols. Water-blown rigid foams were made from polyols with different levels of castor oil replacement. For foams without castor oil and with 25% castor oil replacement, the effects of water added content were studied. Another group of foams made from a castor oil/ glycerol mixture were also prepared to investigate the effects of hydroxyl number. With the help of glycerol, rigid polyurethane foams with 80%-95% castor oil replacement were successfully prepared and showed competitive physical properties. Water-blown flexible foams were made from polyols using different levels of castor oil replacement. At the same time, the influence of cross-linker contents and isocyanate index on flexible foam was studied. Considering the low reaction rate of castor oil during the synthesis of polyurethane, a specific "heated mold" method was applied. Density, compression force deflection (CFD), 50% constant deflection compression (CDC), tear resistance (TR) and resilience were tested to identify the physical properties of flexible polyurethane foams. Results show that castor oil replacement often leads to a high cross-linking density. With 0.5% necessary cross-linker and low isocyanate index, flexible polyurethane foams with 100% castor oil replacement showed a good recovery property and proved to be a suitable alternative to nonrenewable petroleum-based polyols.

Name thesis:degree_name

M.S.

Level thesis:degree_level

Masters

Discipline thesis:degree_discipline

Biological engineering (MU)

Grantor dc:publisher

University of Missouri--Columbia

Year dc:date.issued

2014

Author dc:creator

• Xing, Rui (Biological engineer)

Advisor dc:contributor.advisor

• Hsieh, Fu-hung

• Author supplied: polyurethane, castor oil, biological processing

Language dc:language.iso

eng, English

DOI

https://doi.org/10.32469/10355/44345

OAI identifier oai:identifier

oai:mospace.umsystem.edu:10355/44345