Study of poly (l-lactic acid)/poly (d-lactic acid) stereocomplex as nucleating agent for poly (l- lactic acid) crystallization

Poly (lactic acid) (PLA) is a biodegradable polymer with good renewability and processability. However, it has some drawbacks. The Poly (lactic acid) (PLA) stereocomplex formed via the interaction between optical isomers Poly (L-lactic acid) (PLLA) and Poly (D-lactic acid) (PDLA), provides improvements on PLA thermomechanical properties. To investigate the nucleating effect brought by the PLA stereocomplex, samples of PLLA blended with different content of PDLA are prepared by the solution casting method. With different cooling rates (5, 15, 25 C/min), DSC non-isothermal crystallization experiments are performed. The results suggest that in the presence of the stereocomplex, the PLLA crystallization temperatures are found to be higher than that of pure PLLA. By annealing PLLA at different temperatures with the existence of the stereocomplex, the crystallization process is significantly expedited. Using hot stage polarized microscope, the increasing number of spherulites observed at higher temperature, confirms the enhancement on PLLA nucleation brought by the stereocomplex. Yet, the irregular morphology of crystallites may indicate that the stereocomplex does not promote higher degree of crystallinity. Finally, the saturated nucleating effect is due to the unfavorably high molecular weights of PLLA and PDLA.

Name thesis:degree_name

Master of Science in Materials Science and Engineering - (M.S.)

Discipline thesis:degree_discipline

Committee for the Interdisciplinary Program in Materials Science and Engineering

Year

2013

Author dc:creator

• Lao, Yuan

Contributors dc:contributor

• Costas G. Gogos
• N. M. Ravindra
• Ken Keunhyuk Ahn

• Poly (l- lactic acid) crystallization
• Nucleating agents
• Materials Science and Engineering

Repository record dc:identifier

https://digitalcommons.njit.edu/theses/173

OAI identifier oai:identifier

oai:digitalcommons.njit.edu:theses-1172