{"id":{"repo_id":"vu-aus","oai_identifier":"oai:eprints.vu.edu.au:15565"},"canonical_url":"https://search.dev.ndltd.org/etd/vu-aus/oai:eprints.vu.edu.au:15565","repository":{"repo_id":"vu-aus","name":"Victoria University (Australia)","base_url":"https://vuir.vu.edu.au/cgi/oai2"},"display":{"title":"A study of leaching tests for cement stabilised waste","abstract":"A cement-stabilised waste was subjected to batch, column, and dynamic leaching tests, and the leaching behaviour of arsenic, copper, lead, selenium, and zinc was investigated. Batch tests included the Australian Bottle Leaching Procedure (ABLP, AS 4493.3-1997), Toxicity Characteristic Leaching Procedure (TCLP, USEPA Method 1310); column testing included small columns (internal diameter = 24mm) and a large column (internal diameter = 500mm); and dynamic leaching tests were run with both short (1 hour) and long (4 hour) leachant renewal frequencies. A maximum availability test was used to indicate maximum leaching potential for the metals under investigation.","abstract_html":"A cement-stabilised waste was subjected to batch, column, and dynamic leaching tests, and the leaching behaviour of arsenic, copper, lead, selenium, and zinc was investigated. Batch tests included the Australian Bottle Leaching Procedure (ABLP, AS 4493.3-1997), Toxicity Characteristic Leaching Procedure (TCLP, USEPA Method 1310); column testing included small columns (internal diameter = 24mm) and a large column (internal diameter = 500mm); and dynamic leaching tests were run with both short (1 hour) and long (4 hour) leachant renewal frequencies. A maximum availability test was used to indicate maximum leaching potential for the metals under investigation.","abstract_has_math":false,"creators":["Beard, Jason"],"institution":"Victoria University of Technology","degree_name":"phd","degree_level":"doctoral","degree_discipline":null,"degree_department":null,"school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2002,"date_issued":"2002","date_published":"2002","updated_at":"2026-07-24T06:33:15Z","subjects":["0907 Environmental Engineering","School of Engineering and Science"],"languages":["en"],"rights":[],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":null,"outbound_label":null,"outbound_source":null},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:creator","label":"Author","values":["Beard, Jason"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2002"]},{"key":"dc:date.issued","label":"Date","values":["2002"]},{"key":"dc:publisher.department","label":"Dc Publisher Department","values":["School of Life Sciences and Technology"]},{"key":"dc:publisher.institution","label":"Dc Publisher Institution","values":["Victoria University of Technology"]},{"key":"dc:relation.isreferencedby","label":"Dc Relation Isreferencedby","values":["https://vuir.vu.edu.au/15565/"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.qualificationlevel","label":"Dc Type Qualificationlevel","values":["doctoral"]},{"key":"dc:type.qualificationname","label":"Dc Type Qualificationname","values":["phd"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["0907 Environmental Engineering","School of Engineering and Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["https://vuir.vu.edu.au/15565/5/BEARD%20Jason-thesis_nosignature.pdf"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["A cement-stabilised waste was subjected to batch, column, and dynamic leaching tests, and the leaching behaviour of arsenic, copper, lead, selenium, and zinc was investigated. Batch tests included the Australian Bottle Leaching Procedure (ABLP, AS 4493.3-1997), Toxicity Characteristic Leaching Procedure (TCLP, USEPA Method 1310); column testing included small columns (internal diameter = 24mm) and a large column (internal diameter = 500mm); and dynamic leaching tests were run with both short (1 hour) and long (4 hour) leachant renewal frequencies. A maximum availability test was used to indicate maximum leaching potential for the metals under investigation."]},{"key":"dc:format","label":"Dc Format","values":["text"]},{"key":"dc:title","label":"Title","values":["A study of leaching tests for cement stabilised waste"]}]}],"canonical_facts":{"dc:creator":["Beard, Jason"],"dc:date":["2002"],"dc:date.issued":["2002"],"dc:description.abstract":["A cement-stabilised waste was subjected to batch, column, and dynamic leaching tests, and the leaching behaviour of arsenic, copper, lead, selenium, and zinc was investigated. Batch tests included the Australian Bottle Leaching Procedure (ABLP, AS 4493.3-1997), Toxicity Characteristic Leaching Procedure (TCLP, USEPA Method 1310); column testing included small columns (internal diameter = 24mm) and a large column (internal diameter = 500mm); and dynamic leaching tests were run with both short (1 hour) and long (4 hour) leachant renewal frequencies. A maximum availability test was used to indicate maximum leaching potential for the metals under investigation."],"dc:format":["text"],"dc:identifier.uri":["https://vuir.vu.edu.au/15565/5/BEARD%20Jason-thesis_nosignature.pdf"],"dc:language":["en"],"dc:publisher.department":["School of Life Sciences and Technology"],"dc:publisher.institution":["Victoria University of Technology"],"dc:relation.isreferencedby":["https://vuir.vu.edu.au/15565/"],"dc:subject":["0907 Environmental Engineering","School of Engineering and Science"],"dc:title":["A study of leaching tests for cement stabilised waste"],"dc:type":["Thesis"],"dc:type.qualificationlevel":["doctoral"],"dc:type.qualificationname":["phd"]},"updated_at":"2026-07-24T06:33:15Z"}