{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/91127"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/91127","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Response and failure analysis of a graphite-epoxy laminate containing terminating internal plies","abstract":"A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented.","abstract_html":"A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented.","abstract_has_math":false,"creators":["Kemp, Brian Lee"],"institution":"Virginia Polytechnic Institute and State University","degree_name":"M.S.","degree_level":"masters","degree_discipline":"Aerospace and Ocean Engineering","degree_department":"Aerospace and Ocean Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1985,"date_issued":"1985","date_published":"1985","updated_at":"2026-07-22T22:20:32Z","subjects":[],"languages":["en_US"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/10919/91127","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Aerospace and Ocean Engineering"]},{"key":"dc:creator","label":"Author","values":["Kemp, Brian Lee"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2019-07-03T20:33:54Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2019-07-03T20:33:54Z"]},{"key":"dc:date.issued","label":"Date","values":["1985"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Polytechnic Institute and State University"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Aerospace and Ocean Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en_US"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/91127"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["M.S."]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Response and failure analysis of a graphite-epoxy laminate containing terminating internal plies"]}]}],"canonical_facts":{"dc:contributor.department":["Aerospace and Ocean Engineering"],"dc:creator":["Kemp, Brian Lee"],"dc:date.accessioned":["2019-07-03T20:33:54Z"],"dc:date.available":["2019-07-03T20:33:54Z"],"dc:date.issued":["1985"],"dc:description.abstract":["A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented."],"dc:description.degree":["M.S."],"dc:format.mimetype":["application/pdf"],"dc:identifier.uri":["http://hdl.handle.net/10919/91127"],"dc:language.iso":["en_US"],"dc:publisher":["Virginia Polytechnic Institute and State University"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Response and failure analysis of a graphite-epoxy laminate containing terminating internal plies"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Aerospace and Ocean Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["M.S."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:32Z"}