Al-Ga Sacrificial Anodes: Understanding Performance via Simulation and Modification of Alloy Segregation
Abstract
dc:description.abstractMarine structures must withstand the corrosive effects of salt water in a way that is low cost, reliable, and environmentally friendly. Aluminum satisfies these conditions, and would be a good choice for a sacrificial anode to protect steel structures if it did not passivate. However, various elements can be added to aluminum to prevent this passivation. Currently, Al-Ga alloys are used commercially as sacrificial anodes but their performance is not consistent. In this research, Thermo-Calc software was used to simulate various aspects of the Al-Ga system in an attempt to understand and potentially correct this reliability issue. Simulations showed that gallium segregates to the grain boundaries during solidification and then diffuses back into the grains during cooling to room temperature. Simulations also suggest that faster cooling rates and larger grains cause the potential segregation of gallium at the grain boundaries to remain after cooling. A set of aluminum plus 0.1% weight percent gallium alloy plates were produced with varying cooling rates, along with a control set (cooled slowly in a sand mold). Some samples were later homogenized via annealing. Samples were subjected to a 168 hour long galvanostatic test to assess voltage response. The corrosion performance of samples was found to have both consistent and optimal voltage range when subjected to quick cooling rates followed by annealing. Testing samples at near freezing temperature seems to completely remove optimal corrosion behavior, suggesting that there are multiple causes for the voltage behavior.
Degree
thesis:*- Name thesis:degree_name
- Master of Science
- Level thesis:degree_level
- masters
- Discipline thesis:degree_discipline
- Materials Science and Engineering
- Department dc:contributor.department
- Materials Science and Engineering
- Grantor dc:publisher
- Virginia Tech
- Year dc:date.issued
- 2019
Author and committee
dc:creator, dc:contributor.*- Author dc:creator
-
- Kidd, Michael Scott Jr.
- Chair dc:contributor.committeechair
-
- Druschitz, Alan P.
- Committee members dc:contributor.committeemember
-
- Reynolds, William T. Jr.
- Corcoran, Sean G.
Subjects
dc:subject × 6Rights
dc:rights- Statement dc:rights
-
- In Copyright
- Licence dc:rights.uri
Identifiers
dc:identifier.*- Dc Identifier Other
- vt_gsexam:19193
- OAI identifier oai:identifier
- oai:vtechworks.lib.vt.edu:10919/89066