Influence of Curing Temperature on Strength of Cement-treated Soil and Investigation of Optimum Mix Design for the Wet Method of Deep Mixing

The Deep Mixing Method (DMM) is a widely used, in-situ ground improvement technique that modifies and improves the engineering properties of soil by blending the soil with a cementitious binder. Laboratory specimens were prepared to represent soil improved by the wet method of deep mixing, in which the binder is delivered in the form of a cement-water slurry. To study the influence of curing temperature on the strength of the treated soil, specimens were cured in temperature-controlled water baths for the desired curing time. After curing, unconfined compressive strength (UCS) tests were conducted on the specimens. To investigate the optimum mix design for the wet method of deep mixing, UCS tests were performed to measure the strength of cured specimens, and laboratory miniature vane shear tests were conducted on uncured specimens to measure the undrained shear strength (su), which is used to represent the consistency of the mixture right after mixing. The consistency is important for field mixing because a softer mixture is easier to mix thoroughly. Based on the UCS test results, an equation that can provide a good fit to the strength data of the cured binder-treated soil is proposed. When the curing temperature was changed during curing, the UCS of the specimen cured at a low temperature and then cured at a high temperature was greater than the UCS of the specimen cured at a high temperature first. This seems to be due to different effects of elevated curing temperatures at early and late curing times on the cement reaction rates, such that elevating the curing temperature later produces a more constant reaction rate, which contributes to the reaction efficiency. An optimum mix design that minimizes the amount of binder while satisfying both a target strength of the cured mixture and a target consistency of the uncured mixture can be established by using the fitted equations for UCS and su. The amount of binder required for the optimum mix design increases as the plasticity of the base soil increases and the water content of the base soil (wbase soil) decreases.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Civil Engineering

Department dc:contributor.department

Civil and Environmental Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2019

Author dc:creator

• Ju, Hwanik

Chair dc:contributor.committeechair

• Filz, George M.

Committee members dc:contributor.committeemember

• Green, Russell A.
• Mauldon, Matthew

• Deep Mixing
• Wet Method
• Cement-treated Soil Properties
• Curing Temperature
• Unconfined Compressive Strength
• Consistency
• Optimum Mix Design

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

vt_gsexam:18447

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/86723