Studies on Sintering Silicon Carbide-Nanostructured Ferritic Alloy Composites for Nuclear Applications

Nanostructured ferritic alloy and silicon carbide composite materials (NFA-SiC) were sintered with spark plasma sintering (SPS) method and systematically investigated through X-ray diffraction (XRD), scanning electron microscopy (SEM), as well as density and Vickers hardness tests. Pure NFA, pure SiC, and their composites NFA-SiC with different compositions (2.5 vol% NFA-97.5 vol% SiC, 5 vol% NFA-95 vol% SiC, 97.5 vol% NFA-2.5 vol% SiC, and 95 vol% NFA-5 vol% SiC) were successfully sintered through SPS. In the high-NFA samples, pure NFA and NFA-SiC, minor gamma-Fe phase formation from the main alfa-Fe matrix occurred in pure NFA 950 degree C and 1000 degree C. The densities of the pure NFA and NFA-SiC composites increased with sintering temperature but decreased with SiC content. The Vickers hardness of the pure NFA and NFA-SiC composites was related to density and phase composition. In the high-SiC samples, NFA addition of 2.5 vol% can achieve full densification for the NFA-SiC samples at relative low temperatures. With the increase in sintering temperature, the Vickers hardness of the pure SiC and NFA-SiC composite samples were enhanced. However, the NFA-SiC composites had relative lower hardness than the pure SiC samples. A carbon layer was introduced in the NFA particles to prevent the reaction between NFA and SiC. Results indicated that the carbon layer was effective up to 1050 degree C sintering temperature. Green samples of gradient-structured NFA-SiC composites were successfully fabricated through slip casting of an NFA-SiC co-suspension.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Materials Science and Engineering

Department dc:contributor.department

Materials Science and Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2016

Author dc:creator

• Hu, Zhihao

Chair dc:contributor.committeechair

• Lu, Peizhen

Committee members dc:contributor.committeemember

• Clark, David E.
• Aning, Alexander O.

• nanostructured ferritic alloy (NFA)
• silicon carbide (SiC)
• spark plasma sintering (SPS)
• density
• microstructure
• hardness

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

vt_gsexam:8667

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/81763