{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/77848"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/77848","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Failure processes in unidirectional composite materials","abstract":"Failure processes in unidirectional composite materials subjected to quasi-static tensile load along the fiber direction are investigated. The emphasis in this investigation is to identify the physical processes taking place during the evolution of failure in these materials. An extensive literature review is conducted and the information relevant to the present topic is summarized. The nature of damage growth in five different commercially available composite systems are studied. In-situ scanning electron microscopy is employed for identifying the failure events taking place at the microscopic level. Acoustic emission monitoring is used for estimating the rate of damage growth on a global scale and determining the size of individual failure events. The results of this study have shown the important roles of the matrix material and the interphase in determining the tensile strength of unidirectional composite materials. Several failure modes occurring at the microscopic scale are revealed for the first time. Further, the results indicate that dynamic fracture participates to a significant extent in determining the failure process in these materials. Based on the results of this study the influence of various parameters in determining the composite strength is described.","abstract_html":"Failure processes in unidirectional composite materials subjected to quasi-static tensile load along the fiber direction are investigated. The emphasis in this investigation is to identify the physical processes taking place during the evolution of failure in these materials. An extensive literature review is conducted and the information relevant to the present topic is summarized. The nature of damage growth in five different commercially available composite systems are studied. In-situ scanning electron microscopy is employed for identifying the failure events taking place at the microscopic level. Acoustic emission monitoring is used for estimating the rate of damage growth on a global scale and determining the size of individual failure events. The results of this study have shown the important roles of the matrix material and the interphase in determining the tensile strength of unidirectional composite materials. Several failure modes occurring at the microscopic scale are revealed for the first time. Further, the results indicate that dynamic fracture participates to a significant extent in determining the failure process in these materials. Based on the results of this study the influence of various parameters in determining the composite strength is described.","abstract_has_math":false,"creators":["Sundaresan, Mannur J."],"institution":"Virginia Polytechnic Institute and State University","degree_name":"Ph. D.","degree_level":"doctoral","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Henneke, Edmund G."],"committee_members":["Duke, John C. Jr.","Reddy, Junuthula N.","Reifsnider, Kenneth L.","Smith, C.W."],"year":1988,"date_issued":"1988","date_published":"1988","updated_at":"2026-07-22T22:20:16Z","subjects":[],"languages":["en_US"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/10919/77848","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Henneke, Edmund G."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Duke, John C. Jr.","Reddy, Junuthula N.","Reifsnider, Kenneth L.","Smith, C.W."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Sundaresan, Mannur J."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2017-05-24T18:19:50Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2017-05-24T18:19:50Z"]},{"key":"dc:date.issued","label":"Date","values":["1988"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Polytechnic Institute and State University"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph. D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en_US"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/77848"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Failure processes in unidirectional composite materials subjected to quasi-static tensile load along the fiber direction are investigated. The emphasis in this investigation is to identify the physical processes taking place during the evolution of failure in these materials. An extensive literature review is conducted and the information relevant to the present topic is summarized. The nature of damage growth in five different commercially available composite systems are studied. In-situ scanning electron microscopy is employed for identifying the failure events taking place at the microscopic level. Acoustic emission monitoring is used for estimating the rate of damage growth on a global scale and determining the size of individual failure events. The results of this study have shown the important roles of the matrix material and the interphase in determining the tensile strength of unidirectional composite materials. Several failure modes occurring at the microscopic scale are revealed for the first time. Further, the results indicate that dynamic fracture participates to a significant extent in determining the failure process in these materials. Based on the results of this study the influence of various parameters in determining the composite strength is described."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Ph. D."]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Failure processes in unidirectional composite materials"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Henneke, Edmund G."],"dc:contributor.committeemember":["Duke, John C. Jr.","Reddy, Junuthula N.","Reifsnider, Kenneth L.","Smith, C.W."],"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Sundaresan, Mannur J."],"dc:date.accessioned":["2017-05-24T18:19:50Z"],"dc:date.available":["2017-05-24T18:19:50Z"],"dc:date.issued":["1988"],"dc:description.abstract":["Failure processes in unidirectional composite materials subjected to quasi-static tensile load along the fiber direction are investigated. The emphasis in this investigation is to identify the physical processes taking place during the evolution of failure in these materials. An extensive literature review is conducted and the information relevant to the present topic is summarized. The nature of damage growth in five different commercially available composite systems are studied. In-situ scanning electron microscopy is employed for identifying the failure events taking place at the microscopic level. Acoustic emission monitoring is used for estimating the rate of damage growth on a global scale and determining the size of individual failure events. The results of this study have shown the important roles of the matrix material and the interphase in determining the tensile strength of unidirectional composite materials. Several failure modes occurring at the microscopic scale are revealed for the first time. Further, the results indicate that dynamic fracture participates to a significant extent in determining the failure process in these materials. Based on the results of this study the influence of various parameters in determining the composite strength is described."],"dc:description.degree":["Ph. D."],"dc:format.mimetype":["application/pdf"],"dc:identifier.uri":["http://hdl.handle.net/10919/77848"],"dc:language.iso":["en_US"],"dc:publisher":["Virginia Polytechnic Institute and State University"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Failure processes in unidirectional composite materials"],"dc:type":["Dissertation"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["doctoral"],"thesis:degree_name":["Ph. D."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:16Z"}