Performance Evaluation and Durability Studies of Adhesive Bonds

In this dissertation, four test approaches were developed to characterize the adhesion performance and durability of adhesive bonds for specific applications in areas spanning from structural adhesive joints to popular confectionaries such as chewing gum. In the first chapter, a double cantilever beam (DCB) specimen geometry is proposed for combinatorial fracture studies of structural adhesive bonds. This specimen geometry enabled the characterization of fracture energy vs. bondline thickness trends through fewer tests than those required during a conventional "one at a time" characterization approach, potentially offering a significant reduction in characterization times. The second chapter investigates the adhesive fracture resistance and crack path selection in adhesive joints containing patterns of discreet localized weak interfaces created using physical vapor deposition of copper. In a DCB specimen tested under mode-I conditions, fracture energy within the patterned regions scaled according to a simple rule of mixture, while reverse R-curve and R-curve type trends were observed in the regions surrounding weak interface patterns. Under mixed mode conditions such that bonding surface with patterns is subjected to axial tension, fracture energy did not show R-curve type trends while it was observed that a crack could be made to avoid exceptionally weak interfaces when loaded such that bonding surface with defects is subjected to axial compression. In the third chapter, an adaptation of the probe tack test is proposed to characterize the adhesion behavior of gum cuds. This test method allowed the introduction of substrates with well-defined surface energies and topologies to study their effects on gum cud adhesion. This approach and reported insights could potentially be useful in developing chewing gum formulations that facilitate easy removal of improperly discarded gum cuds from adhering surfaces. In the fourth chapter we highlight a procedure to obtain insights into the long-term performance of silicone sealants designed for load-bearing applications such as solar panel support sealants. Using small strain constitutive tests and time-temperature-superposition principle, thermal shift factors were obtained and successfully used to characterize the creep rupture master curves for specific joint configurations, leading to insights into delayed failures corresponding to three years through experiments carried out in one month.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Macromolecular Science and Engineering

Department dc:contributor.department

Learning Sciences and Technologies

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2014

Author dc:creator

• Ranade, Shantanu Rajendra

Chair dc:contributor.committeechair

• Dillard, David A.

Committee members dc:contributor.committeemember

• Dillard, John G.
• Batra, Romesh C.
• Norris, Ann Marie Walstrom
• Moore, Robert Bowen

• Structural Adhesives
• Double Cantilever Beam Test
• Surface Defects
• Pressure Sensitive Adhesives
• Silicone Sealants
• Fracture Energy
• chewing gum
• Weak Interfaces

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

vt_gsexam:3733

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/64990