{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/63971"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/63971","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Elastic and time dependent matrix cracking in cross-ply composite laminates","abstract":"The effects of time and stress level were investigated in cross-ply laminates to gain more understanding on the damage events in composites. Analytical predictions of the effect of stress level were performed for the case of linear elastic materials. The predictions were based on energy methods and linear elastic fracture mechanics. Damage was simulated with a Monte Carlo numerical scheme. The predicted results corresponded well with experimental data in the literature. Experimental testing was performed on cross-ply laminates to gain a better understanding of the effect of time and rate on matrix cracking. The tests were performed on Kevlar/epoxy and graphite/epoxy [0/90₃]₈ laminates. The results indicate that the stress levels required for matrix cracking are a function of how fast the specimens were loaded. Also, significant time dependent damage was observed in cross-ply laminates which were subjected to sustained loads.","abstract_html":"The effects of time and stress level were investigated in cross-ply laminates to gain more understanding on the damage events in composites. Analytical predictions of the effect of stress level were performed for the case of linear elastic materials. The predictions were based on energy methods and linear elastic fracture mechanics. Damage was simulated with a Monte Carlo numerical scheme. The predicted results corresponded well with experimental data in the literature. Experimental testing was performed on cross-ply laminates to gain a better understanding of the effect of time and rate on matrix cracking. The tests were performed on Kevlar/epoxy and graphite/epoxy [0/90₃]₈ laminates. The results indicate that the stress levels required for matrix cracking are a function of how fast the specimens were loaded. Also, significant time dependent damage was observed in cross-ply laminates which were subjected to sustained loads.","abstract_has_math":false,"creators":["Moore, Robert Hunter"],"institution":"Virginia Polytechnic Institute and State University","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1988,"date_issued":"1988","date_published":"1988","updated_at":"2026-07-22T22:20:43Z","subjects":[],"languages":["en_US"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/10919/63971","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Moore, Robert Hunter"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2015-11-06T19:53:33Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2015-11-06T19:53:33Z"]},{"key":"dc:date.issued","label":"Date","values":["1988"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Polytechnic Institute and State University"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en_US"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/63971"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["The effects of time and stress level were investigated in cross-ply laminates to gain more understanding on the damage events in composites. Analytical predictions of the effect of stress level were performed for the case of linear elastic materials. The predictions were based on energy methods and linear elastic fracture mechanics. Damage was simulated with a Monte Carlo numerical scheme. The predicted results corresponded well with experimental data in the literature. Experimental testing was performed on cross-ply laminates to gain a better understanding of the effect of time and rate on matrix cracking. The tests were performed on Kevlar/epoxy and graphite/epoxy [0/90₃]₈ laminates. The results indicate that the stress levels required for matrix cracking are a function of how fast the specimens were loaded. Also, significant time dependent damage was observed in cross-ply laminates which were subjected to sustained loads."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Elastic and time dependent matrix cracking in cross-ply composite laminates"]}]}],"canonical_facts":{"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Moore, Robert Hunter"],"dc:date.accessioned":["2015-11-06T19:53:33Z"],"dc:date.available":["2015-11-06T19:53:33Z"],"dc:date.issued":["1988"],"dc:description.abstract":["The effects of time and stress level were investigated in cross-ply laminates to gain more understanding on the damage events in composites. Analytical predictions of the effect of stress level were performed for the case of linear elastic materials. The predictions were based on energy methods and linear elastic fracture mechanics. Damage was simulated with a Monte Carlo numerical scheme. The predicted results corresponded well with experimental data in the literature. Experimental testing was performed on cross-ply laminates to gain a better understanding of the effect of time and rate on matrix cracking. The tests were performed on Kevlar/epoxy and graphite/epoxy [0/90₃]₈ laminates. The results indicate that the stress levels required for matrix cracking are a function of how fast the specimens were loaded. Also, significant time dependent damage was observed in cross-ply laminates which were subjected to sustained loads."],"dc:description.degree":["Master of Science"],"dc:format.mimetype":["application/pdf"],"dc:identifier.uri":["http://hdl.handle.net/10919/63971"],"dc:language.iso":["en_US"],"dc:publisher":["Virginia Polytechnic Institute and State University"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Elastic and time dependent matrix cracking in cross-ply composite laminates"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:43Z"}