Studies in vibrofluidized beds and synthesis of silica catalysts

The effect of the solid-circulation rate and pattern as well as the air-gap size on heat-transfer coefficients between a horizontal, cylindrical heater and vibrated beds of Master Beads (spherical alumina) and glass spheres was studied. Solid piles were observed to form at specific bed locations. Solid-circulation paths were directed from the shallowest toward the deepest region of the vibrated bed. For beds in which the solid pile formed above the heating surface, local solid-circulation loops were observed above and below the heater. Air gaps developed at the top and bottom of the cylindrical heater. Heat-transfer coefficients of 140-350 W/m²K in beds of glass spheres and 180-480 W/m²K in beds of Master Beads were determined for a temperature difference of 30°C between the heater and vibrated bed. The trends in the behavior of the heat-transfer coefficient could be explained in terms of a model that accounted for the air-gap size and particle renewal in the layer closest to the heater. Increased solid-circulation rates improved the heat-transfer performance until larger air-gap sizes eventually compromised any increase in solid circulation. The expansion of the interlayer spacing of H-Magadiite (a layered silicic acid) by the introduction of pillars containing silicon atoms was investigated. A trisiloxane and two trichloroorganosilane compounds were used as the pillaring agents. The interlayer space of H-Magadiite was successfully expanded by pillaring with trichloroorganosilanes. The minimum dimensions of the pores that access the interlayer space of the pillared compounds were determined as being 6.2 Å and 9.5 Å (dimensions at perpendicular directions). Pillaring of H-Magadiite at low pH and temperatures close to 0 °C yielded the highest surface areas, e.g., increasing the surface area from 35 to 130-200 m²/g. The pillared compounds were found to be thermally stable up to temperatures of 650°C.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Chemical Engineering

Department dc:contributor.department

Chemical Engineering

Grantor dc:publisher

Virginia Polytechnic Institute and State University

Year dc:date.issued

1987

Author dc:creator

• Sprung, Renato

Chairs dc:contributor.committeechair

• Squires, Arthur M.
• Liu, T.A.

Committee members dc:contributor.committeemember

• Davis, Mark E.
• Diller, Thomas E.
• Wightman, James P.
• Wills, George B.

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Handle dc:identifier.uri

http://hdl.handle.net/10919/49901

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/49901