{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/46290"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/46290","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Processing and properties of composites based on high density polyethylene and thermotropic liquid crystalline polymers","abstract":"This research was concerned with the processing and properties of composites of high density polyethylene (HDPE) and thermotropic liquid crystalline polymers (TLCPs). Strands of HDPE reinforced with TLCPs were generated using a novel dual extruder mixing technique. It was shown that the strength and modulus of the strands improved with increased strand drawing. Post-processing of the blended strands was done by means of compression and injection molding. It was observed that when the fiber aspect ratio dropped, the composite mechanical properties decreased. When pregenerated fibrils were maintained during injection molding at temperatures above the matrix melting point, but below the TLCP melting point, microcomposites were obtained. Microcomposites generated at the lowest temperatures had higher tensile properties than found for in situ composites and similar to glass reinforced HDPE. At 170°C the pregenerated fibers were no longer deformed during injection molding and high aspect ratio fibrils were maintained. The fiber orientation and addition of a compatibilizer were also studied. This study shows it is possible to extrusion blend HDPE with TLCPs and by optimizing the post-processing conditions, to obtain microcomposites with better properties than in situ composites.","abstract_html":"This research was concerned with the processing and properties of composites of high density polyethylene (HDPE) and thermotropic liquid crystalline polymers (TLCPs). Strands of HDPE reinforced with TLCPs were generated using a novel dual extruder mixing technique. It was shown that the strength and modulus of the strands improved with increased strand drawing. Post-processing of the blended strands was done by means of compression and injection molding. It was observed that when the fiber aspect ratio dropped, the composite mechanical properties decreased. When pregenerated fibrils were maintained during injection molding at temperatures above the matrix melting point, but below the TLCP melting point, microcomposites were obtained. Microcomposites generated at the lowest temperatures had higher tensile properties than found for in situ composites and similar to glass reinforced HDPE. At 170°C the pregenerated fibers were no longer deformed during injection molding and high aspect ratio fibrils were maintained. The fiber orientation and addition of a compatibilizer were also studied. This study shows it is possible to extrusion blend HDPE with TLCPs and by optimizing the post-processing conditions, to obtain microcomposites with better properties than in situ composites.","abstract_has_math":false,"creators":["Wesselingh, Marjan"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Chemical Engineering","degree_department":"Chemical Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1995,"date_issued":"1995","date_published":"1995","updated_at":"2026-07-22T22:18:53Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-12172008-063352"],"render_values":[{"text":"etd-12172008-063352","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/46290","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Chemical Engineering"]},{"key":"dc:creator","label":"Author","values":["Wesselingh, Marjan"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:51:55Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:51:55Z","2008-12-17"]},{"key":"dc:date.issued","label":"Date","values":["1995"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Chemical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-12172008-063352"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/46290"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["This research was concerned with the processing and properties of composites of high density polyethylene (HDPE) and thermotropic liquid crystalline polymers (TLCPs). Strands of HDPE reinforced with TLCPs were generated using a novel dual extruder mixing technique. It was shown that the strength and modulus of the strands improved with increased strand drawing. Post-processing of the blended strands was done by means of compression and injection molding. It was observed that when the fiber aspect ratio dropped, the composite mechanical properties decreased. When pregenerated fibrils were maintained during injection molding at temperatures above the matrix melting point, but below the TLCP melting point, microcomposites were obtained. Microcomposites generated at the lowest temperatures had higher tensile properties than found for in situ composites and similar to glass reinforced HDPE. At 170°C the pregenerated fibers were no longer deformed during injection molding and high aspect ratio fibrils were maintained. The fiber orientation and addition of a compatibilizer were also studied. This study shows it is possible to extrusion blend HDPE with TLCPs and by optimizing the post-processing conditions, to obtain microcomposites with better properties than in situ composites."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Processing and properties of composites based on high density polyethylene and thermotropic liquid crystalline polymers"]}]}],"canonical_facts":{"dc:contributor.department":["Chemical Engineering"],"dc:creator":["Wesselingh, Marjan"],"dc:date.accessioned":["2014-03-14T21:51:55Z"],"dc:date.available":["2014-03-14T21:51:55Z","2008-12-17"],"dc:date.issued":["1995"],"dc:description.abstract":["This research was concerned with the processing and properties of composites of high density polyethylene (HDPE) and thermotropic liquid crystalline polymers (TLCPs). Strands of HDPE reinforced with TLCPs were generated using a novel dual extruder mixing technique. It was shown that the strength and modulus of the strands improved with increased strand drawing. Post-processing of the blended strands was done by means of compression and injection molding. It was observed that when the fiber aspect ratio dropped, the composite mechanical properties decreased. When pregenerated fibrils were maintained during injection molding at temperatures above the matrix melting point, but below the TLCP melting point, microcomposites were obtained. Microcomposites generated at the lowest temperatures had higher tensile properties than found for in situ composites and similar to glass reinforced HDPE. At 170°C the pregenerated fibers were no longer deformed during injection molding and high aspect ratio fibrils were maintained. The fiber orientation and addition of a compatibilizer were also studied. This study shows it is possible to extrusion blend HDPE with TLCPs and by optimizing the post-processing conditions, to obtain microcomposites with better properties than in situ composites."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-12172008-063352"],"dc:identifier.uri":["http://hdl.handle.net/10919/46290"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Processing and properties of composites based on high density polyethylene and thermotropic liquid crystalline polymers"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Chemical Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:53Z"}