{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/44913"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/44913","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"The evaluation of corrosion inhibitors for the repair and rehabilitation of reinforced concrete bridge components","abstract":"In 1991, seven corrosion inhibitors, surface applied liquids and concrete admixtures, were identified as promising for the repair of reinforced concrete structures subject to chloride induced corrosion. Small scale (1 ft.²) reinforced concrete specimens were cast to evaluate the inhibitors effectiveness. A treatment matrix was established to evaluate the inhibitors performance on three ranges of corrosion activity and evaluate the effect of application time and drying. Corrosion rate measurements taken with a linear polarization device were used to monitor the inhibitors effectiveness. The effect of the admixtures on the concrete properties, and the effect of the surface applied inhibitors on the overlay bond strength were evaluated. Rapid freeze-thaw tests were conducted to estimate the durability of the inhibitor modified concrete. Three combinations of inhibitors were identified for large scale testing after ten months of accelerated chloride exposure. The larger specimens, removed from an actual bridge deck, were treated to test the effective inhibitors field application techniques. Service life estimates were made for the two combinations of inhibitors which were most effective to aid the engineer in assessing the inhibitors cost effectiveness.","abstract_html":"In 1991, seven corrosion inhibitors, surface applied liquids and concrete admixtures, were identified as promising for the repair of reinforced concrete structures subject to chloride induced corrosion. Small scale (1 ft.²) reinforced concrete specimens were cast to evaluate the inhibitors effectiveness. A treatment matrix was established to evaluate the inhibitors performance on three ranges of corrosion activity and evaluate the effect of application time and drying. Corrosion rate measurements taken with a linear polarization device were used to monitor the inhibitors effectiveness. The effect of the admixtures on the concrete properties, and the effect of the surface applied inhibitors on the overlay bond strength were evaluated. Rapid freeze-thaw tests were conducted to estimate the durability of the inhibitor modified concrete. Three combinations of inhibitors were identified for large scale testing after ten months of accelerated chloride exposure. The larger specimens, removed from an actual bridge deck, were treated to test the effective inhibitors field application techniques. Service life estimates were made for the two combinations of inhibitors which were most effective to aid the engineer in assessing the inhibitors cost effectiveness.","abstract_has_math":false,"creators":["Prowell, Brian D."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Civil Engineering","degree_department":"Civil Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1992,"date_issued":"1992","date_published":"1992","updated_at":"2026-07-22T22:20:34Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-09292009-020105"],"render_values":[{"text":"etd-09292009-020105","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/44913","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Civil Engineering"]},{"key":"dc:creator","label":"Author","values":["Prowell, Brian D."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:46:32Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:46:32Z","2009-09-29"]},{"key":"dc:date.issued","label":"Date","values":["1992"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Civil Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-09292009-020105"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/44913"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["In 1991, seven corrosion inhibitors, surface applied liquids and concrete admixtures, were identified as promising for the repair of reinforced concrete structures subject to chloride induced corrosion. Small scale (1 ft.²) reinforced concrete specimens were cast to evaluate the inhibitors effectiveness. A treatment matrix was established to evaluate the inhibitors performance on three ranges of corrosion activity and evaluate the effect of application time and drying. Corrosion rate measurements taken with a linear polarization device were used to monitor the inhibitors effectiveness. The effect of the admixtures on the concrete properties, and the effect of the surface applied inhibitors on the overlay bond strength were evaluated. Rapid freeze-thaw tests were conducted to estimate the durability of the inhibitor modified concrete. Three combinations of inhibitors were identified for large scale testing after ten months of accelerated chloride exposure. The larger specimens, removed from an actual bridge deck, were treated to test the effective inhibitors field application techniques. Service life estimates were made for the two combinations of inhibitors which were most effective to aid the engineer in assessing the inhibitors cost effectiveness."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["The evaluation of corrosion inhibitors for the repair and rehabilitation of reinforced concrete bridge components"]}]}],"canonical_facts":{"dc:contributor.department":["Civil Engineering"],"dc:creator":["Prowell, Brian D."],"dc:date.accessioned":["2014-03-14T21:46:32Z"],"dc:date.available":["2014-03-14T21:46:32Z","2009-09-29"],"dc:date.issued":["1992"],"dc:description.abstract":["In 1991, seven corrosion inhibitors, surface applied liquids and concrete admixtures, were identified as promising for the repair of reinforced concrete structures subject to chloride induced corrosion. Small scale (1 ft.²) reinforced concrete specimens were cast to evaluate the inhibitors effectiveness. A treatment matrix was established to evaluate the inhibitors performance on three ranges of corrosion activity and evaluate the effect of application time and drying. Corrosion rate measurements taken with a linear polarization device were used to monitor the inhibitors effectiveness. The effect of the admixtures on the concrete properties, and the effect of the surface applied inhibitors on the overlay bond strength were evaluated. Rapid freeze-thaw tests were conducted to estimate the durability of the inhibitor modified concrete. Three combinations of inhibitors were identified for large scale testing after ten months of accelerated chloride exposure. The larger specimens, removed from an actual bridge deck, were treated to test the effective inhibitors field application techniques. Service life estimates were made for the two combinations of inhibitors which were most effective to aid the engineer in assessing the inhibitors cost effectiveness."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-09292009-020105"],"dc:identifier.uri":["http://hdl.handle.net/10919/44913"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["The evaluation of corrosion inhibitors for the repair and rehabilitation of reinforced concrete bridge components"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Civil Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:34Z"}