{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/44828"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/44828","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Friction, wear and lubrication of a poly(2-hydroxyethyl methacrylate) hydrogel","abstract":"Poly(2-hydroxyethyl) methacrylate, (polyHEMA), hydrogels are synthesized for tribological study to investigate their potential for use as synthetic articular cartilage. A four factor, two level designed experiment was performed to evaluate friction and wear of polyHEMA. Tests were carried out using a friction and wear test device developed for biotribology research. The geometry consisted of a ball on flat; 6mm stainless steel ball and flat polyHEMA discs. Test factors were load, lubrication, hydration and material crosslink density. Linear oscillating sliding contact tests were performed on each polyHEMA disc for approximately 30 minutes per test. Friction coefficients found ranged from 0.05 to 1.7. Linear wear measured ranged from 0.02 mm to 1.32 mm.","abstract_html":"Poly(2-hydroxyethyl) methacrylate, (polyHEMA), hydrogels are synthesized for tribological study to investigate their potential for use as synthetic articular cartilage. A four factor, two level designed experiment was performed to evaluate friction and wear of polyHEMA. Tests were carried out using a friction and wear test device developed for biotribology research. The geometry consisted of a ball on flat; 6mm stainless steel ball and flat polyHEMA discs. Test factors were load, lubrication, hydration and material crosslink density. Linear oscillating sliding contact tests were performed on each polyHEMA disc for approximately 30 minutes per test. Friction coefficients found ranged from 0.05 to 1.7. Linear wear measured ranged from 0.02 mm to 1.32 mm.","abstract_has_math":false,"creators":["Freeman, Mark E."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Mechanical Engineering","degree_department":"Mechanical Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":["Furey, Michael J."],"committee_members":["Eiss, Norman S. Jr.","Love, Brian J."],"year":1996,"date_issued":"1996-12-05","date_published":"1996-12-05","updated_at":"2026-07-22T22:18:52Z","subjects":["synthetic articular cartilage"],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-09182008-063516"],"render_values":[{"text":"etd-09182008-063516","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/44828","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Furey, Michael J."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Eiss, Norman S. Jr.","Love, Brian J."]},{"key":"dc:contributor.department","label":"Department","values":["Mechanical Engineering"]},{"key":"dc:creator","label":"Author","values":["Freeman, Mark E."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:46:03Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:46:03Z","2008-09-18"]},{"key":"dc:date.issued","label":"Date","values":["1996-12-05"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Mechanical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["synthetic articular cartilage"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-09182008-063516"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/44828"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Poly(2-hydroxyethyl) methacrylate, (polyHEMA), hydrogels are synthesized for tribological study to investigate their potential for use as synthetic articular cartilage. A four factor, two level designed experiment was performed to evaluate friction and wear of polyHEMA. Tests were carried out using a friction and wear test device developed for biotribology research. The geometry consisted of a ball on flat; 6mm stainless steel ball and flat polyHEMA discs. Test factors were load, lubrication, hydration and material crosslink density. Linear oscillating sliding contact tests were performed on each polyHEMA disc for approximately 30 minutes per test. Friction coefficients found ranged from 0.05 to 1.7. Linear wear measured ranged from 0.02 mm to 1.32 mm."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Friction, wear and lubrication of a poly(2-hydroxyethyl methacrylate) hydrogel"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Furey, Michael J."],"dc:contributor.committeemember":["Eiss, Norman S. Jr.","Love, Brian J."],"dc:contributor.department":["Mechanical Engineering"],"dc:creator":["Freeman, Mark E."],"dc:date.accessioned":["2014-03-14T21:46:03Z"],"dc:date.available":["2014-03-14T21:46:03Z","2008-09-18"],"dc:date.issued":["1996-12-05"],"dc:description.abstract":["Poly(2-hydroxyethyl) methacrylate, (polyHEMA), hydrogels are synthesized for tribological study to investigate their potential for use as synthetic articular cartilage. A four factor, two level designed experiment was performed to evaluate friction and wear of polyHEMA. Tests were carried out using a friction and wear test device developed for biotribology research. The geometry consisted of a ball on flat; 6mm stainless steel ball and flat polyHEMA discs. Test factors were load, lubrication, hydration and material crosslink density. Linear oscillating sliding contact tests were performed on each polyHEMA disc for approximately 30 minutes per test. Friction coefficients found ranged from 0.05 to 1.7. Linear wear measured ranged from 0.02 mm to 1.32 mm."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-09182008-063516"],"dc:identifier.uri":["http://hdl.handle.net/10919/44828"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["synthetic articular cartilage"],"dc:title":["Friction, wear and lubrication of a poly(2-hydroxyethyl methacrylate) hydrogel"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Mechanical Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:52Z"}