The effect of cooling rate on toughness and crystallinity in poly(ether ketone ketone) (PEKK)/G30-500 composites

Six poly(ether ketone ketone)/carbon composite panels were manufactured from powder coated towpreg. All six panels were initially processed using a hot press equipped with controlled cooling. Four of the panels were used to investigate the effect of cooling rate on crystallinity. A fifth panel was used to investigate the effect of annealing the composite after completion of the standard fabrication process. The sixth panel was used to investigate changes in toughness due to manufacturing towpreg with polymer that had been reclaimed from the towpreg fabrication system’s air cleaner. Cooling rates of 2°C/min, 4°C/min, 6°C/min, and 8°C/min resulted in composites with crystallinities of 33%, 27%, 24%, and 23%, respectively. The principal investigation of the effect of cooling rate on crystallinity and mode I and mode II strain energy release rates, G_Ic and G_IIc, respectively, showed that G_Ic and G_IIc values increase with increasing cooling rate. Comparison of the toughness values as a function of crystallinity showed that the dependence of toughness on crystallinity is approximately equivalent to the dependence of toughness on cooling rate. Comparison of the data from the annealed panel to that from the analogous principal panel showed that annealing increased the crystallinity and decreased the mode I strain energy release rate. There was no effect, however, on the mode II strain energy release rate. Comparison of the data from the panel made with reclaimed polymer to that from its analogous principal panel showed that the reclaimed polymer panel had equivalent crystallinity and G_Ic values. On the other hand, the G_IIc values in this panel were lower than in the analogous principal panel.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Materials Science and Engineering

Department dc:contributor.department

Materials Science and Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

1996

Author dc:creator

• Davis, Kedzie

Chair dc:contributor.committeechair

• Loos, Alfred C.

Committee members dc:contributor.committeemember

• Wilkes, Garth L.
• Kander, Ronald C.

• mode I and mode II strain energy release rates
• interlaminar fracture toughness
• carbon fiber composites
• PEKK
• degree of crystallinity

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Dc Identifier Other

etd-09182008-063310

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/44807