{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/44176"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/44176","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Optimal design and testing of laminated specimens to evaluate competing composite failure criteria","abstract":"Optimization methods are used to find areas of maximum disagreement between the failure criteria of Tsai and Hart-Smith. The Tsai criterion is quadratic in the stresses and employs a selective and progressive ply-by-ply degradation scheme to predict ultimate load. Hart-Smith’s criterion is based on a fiber shear failure of the fibers and also predicts ultimate load. Both compression-compression and tension-shear combinations are identified as areas of large difference in predicted failure loads. Graphite-epoxy specimens are designed to maximize the difference in the failure loads computed from the two criteria under uniaxial tension. Both on-axis and ten-degree off-axis specimens are designed and tested. The laminates that maximize the difference in these criteria exploit the manner in which they treat the effect of in-plane shear on the failure prediction. Test results indicate little difference in the failure prediction for the on-axis test. However, the off-axis tests show that the Tsai criterion predicts failure much closer to the test results.","abstract_html":"Optimization methods are used to find areas of maximum disagreement between the failure criteria of Tsai and Hart-Smith. The Tsai criterion is quadratic in the stresses and employs a selective and progressive ply-by-ply degradation scheme to predict ultimate load. Hart-Smith’s criterion is based on a fiber shear failure of the fibers and also predicts ultimate load. Both compression-compression and tension-shear combinations are identified as areas of large difference in predicted failure loads. Graphite-epoxy specimens are designed to maximize the difference in the failure loads computed from the two criteria under uniaxial tension. Both on-axis and ten-degree off-axis specimens are designed and tested. The laminates that maximize the difference in these criteria exploit the manner in which they treat the effect of in-plane shear on the failure prediction. Test results indicate little difference in the failure prediction for the on-axis test. However, the off-axis tests show that the Tsai criterion predicts failure much closer to the test results.","abstract_has_math":false,"creators":["Wamelen, Arend Andries van"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Aerospace Engineering","degree_department":"Aerospace Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1993,"date_issued":"1993","date_published":"1993","updated_at":"2026-07-22T22:19:48Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-08042009-040517"],"render_values":[{"text":"etd-08042009-040517","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/44176","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Aerospace Engineering"]},{"key":"dc:creator","label":"Author","values":["Wamelen, Arend Andries van"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:42:16Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:42:16Z","2009-08-04"]},{"key":"dc:date.issued","label":"Date","values":["1993"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Aerospace Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-08042009-040517"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/44176"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Optimization methods are used to find areas of maximum disagreement between the failure criteria of Tsai and Hart-Smith. The Tsai criterion is quadratic in the stresses and employs a selective and progressive ply-by-ply degradation scheme to predict ultimate load. Hart-Smith’s criterion is based on a fiber shear failure of the fibers and also predicts ultimate load. Both compression-compression and tension-shear combinations are identified as areas of large difference in predicted failure loads. Graphite-epoxy specimens are designed to maximize the difference in the failure loads computed from the two criteria under uniaxial tension. Both on-axis and ten-degree off-axis specimens are designed and tested. The laminates that maximize the difference in these criteria exploit the manner in which they treat the effect of in-plane shear on the failure prediction. Test results indicate little difference in the failure prediction for the on-axis test. However, the off-axis tests show that the Tsai criterion predicts failure much closer to the test results."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Optimal design and testing of laminated specimens to evaluate competing composite failure criteria"]}]}],"canonical_facts":{"dc:contributor.department":["Aerospace Engineering"],"dc:creator":["Wamelen, Arend Andries van"],"dc:date.accessioned":["2014-03-14T21:42:16Z"],"dc:date.available":["2014-03-14T21:42:16Z","2009-08-04"],"dc:date.issued":["1993"],"dc:description.abstract":["Optimization methods are used to find areas of maximum disagreement between the failure criteria of Tsai and Hart-Smith. The Tsai criterion is quadratic in the stresses and employs a selective and progressive ply-by-ply degradation scheme to predict ultimate load. Hart-Smith’s criterion is based on a fiber shear failure of the fibers and also predicts ultimate load. Both compression-compression and tension-shear combinations are identified as areas of large difference in predicted failure loads. Graphite-epoxy specimens are designed to maximize the difference in the failure loads computed from the two criteria under uniaxial tension. Both on-axis and ten-degree off-axis specimens are designed and tested. The laminates that maximize the difference in these criteria exploit the manner in which they treat the effect of in-plane shear on the failure prediction. Test results indicate little difference in the failure prediction for the on-axis test. However, the off-axis tests show that the Tsai criterion predicts failure much closer to the test results."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-08042009-040517"],"dc:identifier.uri":["http://hdl.handle.net/10919/44176"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Optimal design and testing of laminated specimens to evaluate competing composite failure criteria"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Aerospace Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:19:48Z"}