{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/43950"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/43950","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Theory of ultrasonic diffraction by damage developed in thin laminated composites","abstract":"This thesis provides a general theory of the diffraction of ultrasonic waves. The theory is then used to find the apparent attenuation which would result if certain damage states (transverse cracks and delaminations) are introduced into a graphite/epoxy laminate through which the ultrasonic wave passes. and [0, ±45, 90]s) is presented which shows changes in the apparent attenuation of, about 1 dB. These changes generally occur at loads which correspond to the range predicted for the formation of the above mentioned damage. Though no exact correlation between theoretical and experimental results is given, the predicted changes in the attenuation for several simple and common damage states are well within the range of experimental values. It is hoped that the technique described herein can be further developed and used to detect the formation and growth of damage in composite specimens in regions not readily visible by conventional techniques.","abstract_html":"This thesis provides a general theory of the diffraction of ultrasonic waves. The theory is then used to find the apparent attenuation which would result if certain damage states (transverse cracks and delaminations) are introduced into a graphite/epoxy laminate through which the ultrasonic wave passes. and [0, ±45, 90]s) is presented which shows changes in the apparent attenuation of, about 1 dB. These changes generally occur at loads which correspond to the range predicted for the formation of the above mentioned damage. Though no exact correlation between theoretical and experimental results is given, the predicted changes in the attenuation for several simple and common damage states are well within the range of experimental values. It is hoped that the technique described herein can be further developed and used to detect the formation and growth of damage in composite specimens in regions not readily visible by conventional techniques.","abstract_has_math":false,"creators":["Hayford, Donald Thomas"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Henneke, Edmund G. II"],"committee_members":["Reifsnider, Kenneth L.","Stinchcomb, Wayne W.","Frederick, Daniel"],"year":1977,"date_issued":"1977-09-05","date_published":"1977-09-05","updated_at":"2026-07-22T22:20:25Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07282010-020242"],"render_values":[{"text":"etd-07282010-020242","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/43950","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Henneke, Edmund G. II"]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Reifsnider, Kenneth L.","Stinchcomb, Wayne W.","Frederick, Daniel"]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Hayford, Donald Thomas"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:41:25Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:41:25Z","2010-07-28"]},{"key":"dc:date.issued","label":"Date","values":["1977-09-05"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07282010-020242"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/43950"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["This thesis provides a general theory of the diffraction of ultrasonic waves. The theory is then used to find the apparent attenuation which would result if certain damage states (transverse cracks and delaminations) are introduced into a graphite/epoxy laminate through which the ultrasonic wave passes. and [0, ±45, 90]s) is presented which shows changes in the apparent attenuation of, about 1 dB. These changes generally occur at loads which correspond to the range predicted for the formation of the above mentioned damage. Though no exact correlation between theoretical and experimental results is given, the predicted changes in the attenuation for several simple and common damage states are well within the range of experimental values. It is hoped that the technique described herein can be further developed and used to detect the formation and growth of damage in composite specimens in regions not readily visible by conventional techniques."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Theory of ultrasonic diffraction by damage developed in thin laminated composites"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Henneke, Edmund G. II"],"dc:contributor.committeemember":["Reifsnider, Kenneth L.","Stinchcomb, Wayne W.","Frederick, Daniel"],"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Hayford, Donald Thomas"],"dc:date.accessioned":["2014-03-14T21:41:25Z"],"dc:date.available":["2014-03-14T21:41:25Z","2010-07-28"],"dc:date.issued":["1977-09-05"],"dc:description.abstract":["This thesis provides a general theory of the diffraction of ultrasonic waves. The theory is then used to find the apparent attenuation which would result if certain damage states (transverse cracks and delaminations) are introduced into a graphite/epoxy laminate through which the ultrasonic wave passes. and [0, ±45, 90]s) is presented which shows changes in the apparent attenuation of, about 1 dB. These changes generally occur at loads which correspond to the range predicted for the formation of the above mentioned damage. Though no exact correlation between theoretical and experimental results is given, the predicted changes in the attenuation for several simple and common damage states are well within the range of experimental values. It is hoped that the technique described herein can be further developed and used to detect the formation and growth of damage in composite specimens in regions not readily visible by conventional techniques."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-07282010-020242"],"dc:identifier.uri":["http://hdl.handle.net/10919/43950"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Theory of ultrasonic diffraction by damage developed in thin laminated composites"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:25Z"}