{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/43831"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/43831","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Mechanical behavior and damage mechanisms of woven graphite-polyimide composite materials","abstract":"The behavior of 8-harness satin woven Celion 3000/PMR-15 graphite-polyimide was experimentally investigated. Unnotched and center-notched specimens from (0)₁₅, (0)₂₂, and (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminates were tested. Material properties were measured and damage development documented under monotonic tension, sustained incremental tension, and tension-tension fatigue loading. Damage evaluation techniques included stiffness monitoring, penetrant-enhanced X-ray radiography, laminate deply, and residual strength measurement. Material properties of the woven graphite-polyimide were comparable to those of woven graphite-epoxy. Damage development in woven graphite-polyimide was quite different than in non-woven graphite-epoxy. Matrix cracking was denser and delamination less extensive in the graphite-polyimide material system, and as a result, increases in notched residual tensile strength were much lower. A ply level failure theory was used to successfully predict the notched tensile strength of the (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminate based on experimental data from the (0)₂₂ laminate. A simple method was used to simulate fatigue damage in a (0)₂₂ notched specimen to predict residual strength as a function of fatigue life. The advantages and disadvantages of the ply level failure theory used in this study are discussed.","abstract_html":"The behavior of 8-harness satin woven Celion 3000/PMR-15 graphite-polyimide was experimentally investigated. Unnotched and center-notched specimens from (0)₁₅, (0)₂₂, and (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminates were tested. Material properties were measured and damage development documented under monotonic tension, sustained incremental tension, and tension-tension fatigue loading. Damage evaluation techniques included stiffness monitoring, penetrant-enhanced X-ray radiography, laminate deply, and residual strength measurement. Material properties of the woven graphite-polyimide were comparable to those of woven graphite-epoxy. Damage development in woven graphite-polyimide was quite different than in non-woven graphite-epoxy. Matrix cracking was denser and delamination less extensive in the graphite-polyimide material system, and as a result, increases in notched residual tensile strength were much lower. A ply level failure theory was used to successfully predict the notched tensile strength of the (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminate based on experimental data from the (0)₂₂ laminate. A simple method was used to simulate fatigue damage in a (0)₂₂ notched specimen to predict residual strength as a function of fatigue life. The advantages and disadvantages of the ply level failure theory used in this study are discussed.","abstract_has_math":false,"creators":["Wagnecz, Linda"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1987,"date_issued":"1987","date_published":"1987","updated_at":"2026-07-22T22:20:27Z","subjects":[],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07212010-020200"],"render_values":[{"text":"etd-07212010-020200","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/43831","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Wagnecz, Linda"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:40:56Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:40:56Z","2010-07-21"]},{"key":"dc:date.issued","label":"Date","values":["1987"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07212010-020200"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/43831"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["The behavior of 8-harness satin woven Celion 3000/PMR-15 graphite-polyimide was experimentally investigated. Unnotched and center-notched specimens from (0)₁₅, (0)₂₂, and (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminates were tested. Material properties were measured and damage development documented under monotonic tension, sustained incremental tension, and tension-tension fatigue loading. Damage evaluation techniques included stiffness monitoring, penetrant-enhanced X-ray radiography, laminate deply, and residual strength measurement. Material properties of the woven graphite-polyimide were comparable to those of woven graphite-epoxy. Damage development in woven graphite-polyimide was quite different than in non-woven graphite-epoxy. Matrix cracking was denser and delamination less extensive in the graphite-polyimide material system, and as a result, increases in notched residual tensile strength were much lower. A ply level failure theory was used to successfully predict the notched tensile strength of the (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminate based on experimental data from the (0)₂₂ laminate. A simple method was used to simulate fatigue damage in a (0)₂₂ notched specimen to predict residual strength as a function of fatigue life. The advantages and disadvantages of the ply level failure theory used in this study are discussed."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Mechanical behavior and damage mechanisms of woven graphite-polyimide composite materials"]}]}],"canonical_facts":{"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Wagnecz, Linda"],"dc:date.accessioned":["2014-03-14T21:40:56Z"],"dc:date.available":["2014-03-14T21:40:56Z","2010-07-21"],"dc:date.issued":["1987"],"dc:description.abstract":["The behavior of 8-harness satin woven Celion 3000/PMR-15 graphite-polyimide was experimentally investigated. Unnotched and center-notched specimens from (0)₁₅, (0)₂₂, and (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminates were tested. Material properties were measured and damage development documented under monotonic tension, sustained incremental tension, and tension-tension fatigue loading. Damage evaluation techniques included stiffness monitoring, penetrant-enhanced X-ray radiography, laminate deply, and residual strength measurement. Material properties of the woven graphite-polyimide were comparable to those of woven graphite-epoxy. Damage development in woven graphite-polyimide was quite different than in non-woven graphite-epoxy. Matrix cracking was denser and delamination less extensive in the graphite-polyimide material system, and as a result, increases in notched residual tensile strength were much lower. A ply level failure theory was used to successfully predict the notched tensile strength of the (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminate based on experimental data from the (0)₂₂ laminate. A simple method was used to simulate fatigue damage in a (0)₂₂ notched specimen to predict residual strength as a function of fatigue life. The advantages and disadvantages of the ply level failure theory used in this study are discussed."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-07212010-020200"],"dc:identifier.uri":["http://hdl.handle.net/10919/43831"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Mechanical behavior and damage mechanisms of woven graphite-polyimide composite materials"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:27Z"}