{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/43617"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/43617","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Characterization of the wood/isocyanate bondline","abstract":"Polymeric diphenylmethane diisocyanate, pMDI, is a wood adhesive that provides excellent composite board properties. Much is unknown about the specific mechanism of pMDI/wood adhesion under conditions that are typical of wood gluing operations. The present research describes the use of ¹⁵N cross-polarization, magic-angle spinning (CP/MAS) NMR as a technique for probing the cure chemistry and bondline morphology of pMDI-bonded wood composites. A 99% ¹⁵N-enriched pMDI resin with desirable adhesive properties was synthesized. A series of model cellulose/¹⁵N-pMDI composites, cured as a function of cellulose precure moisture content, were tested prior to solid wood composites in order to test the feasibility of this technique. Solid wood/¹⁵N-pMDI composites were then cured as a function of wood precure moisture content, cure temperature, and cure time. The ¹⁵N CP/MAS NMR spectra clearly show the dominance of the isocyanate/water reaction on the cure chemistry of all composites tested, both cellulose and solid wood. Four prominent resonances are observed in each spectrum: residual isocyanate, polyurea, and the amide and imide nitrogens of biuret type structures. Different trends in the relative intensities of these resonances are observed as a function of the press variables. Significant amounts of urethane formation are not detected; however, low amounts could be obscured by signal overlap. Relaxation studies using variable contact time experiments were complicated by excessively long cross-polarization rates for nonprotonated nitrogens. However, experiments using variable spin lock times prior to fixed contact periods indicate that the cured resin in these composites is probably a homogeneous continuum. The utility of ¹⁵N CP/MAS NMR for elucidating fine structural and morphological information from complex isocyanate-cured wood composites is clearly demonstrated.","abstract_html":"Polymeric diphenylmethane diisocyanate, pMDI, is a wood adhesive that provides excellent composite board properties. Much is unknown about the specific mechanism of pMDI/wood adhesion under conditions that are typical of wood gluing operations. The present research describes the use of ¹⁵N cross-polarization, magic-angle spinning (CP/MAS) NMR as a technique for probing the cure chemistry and bondline morphology of pMDI-bonded wood composites. A 99% ¹⁵N-enriched pMDI resin with desirable adhesive properties was synthesized. A series of model cellulose/¹⁵N-pMDI composites, cured as a function of cellulose precure moisture content, were tested prior to solid wood composites in order to test the feasibility of this technique. Solid wood/¹⁵N-pMDI composites were then cured as a function of wood precure moisture content, cure temperature, and cure time. The ¹⁵N CP/MAS NMR spectra clearly show the dominance of the isocyanate/water reaction on the cure chemistry of all composites tested, both cellulose and solid wood. Four prominent resonances are observed in each spectrum: residual isocyanate, polyurea, and the amide and imide nitrogens of biuret type structures. Different trends in the relative intensities of these resonances are observed as a function of the press variables. Significant amounts of urethane formation are not detected; however, low amounts could be obscured by signal overlap. Relaxation studies using variable contact time experiments were complicated by excessively long cross-polarization rates for nonprotonated nitrogens. However, experiments using variable spin lock times prior to fixed contact periods indicate that the cured resin in these composites is probably a homogeneous continuum. The utility of ¹⁵N CP/MAS NMR for elucidating fine structural and morphological information from complex isocyanate-cured wood composites is clearly demonstrated.","abstract_has_math":false,"creators":["Wendler, Steven L."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Wood Science and Forest Products","degree_department":"Wood Science and Forest Products","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1994,"date_issued":"1994","date_published":"1994","updated_at":"2026-07-22T22:20:43Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07102009-040325"],"render_values":[{"text":"etd-07102009-040325","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/43617","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Wood Science and Forest Products"]},{"key":"dc:creator","label":"Author","values":["Wendler, Steven L."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:39:54Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:39:54Z","2009-07-10"]},{"key":"dc:date.issued","label":"Date","values":["1994"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Wood Science and Forest Products"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-07102009-040325"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/43617"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Polymeric diphenylmethane diisocyanate, pMDI, is a wood adhesive that provides excellent composite board properties. Much is unknown about the specific mechanism of pMDI/wood adhesion under conditions that are typical of wood gluing operations. The present research describes the use of ¹⁵N cross-polarization, magic-angle spinning (CP/MAS) NMR as a technique for probing the cure chemistry and bondline morphology of pMDI-bonded wood composites. A 99% ¹⁵N-enriched pMDI resin with desirable adhesive properties was synthesized. A series of model cellulose/¹⁵N-pMDI composites, cured as a function of cellulose precure moisture content, were tested prior to solid wood composites in order to test the feasibility of this technique. Solid wood/¹⁵N-pMDI composites were then cured as a function of wood precure moisture content, cure temperature, and cure time. The ¹⁵N CP/MAS NMR spectra clearly show the dominance of the isocyanate/water reaction on the cure chemistry of all composites tested, both cellulose and solid wood. Four prominent resonances are observed in each spectrum: residual isocyanate, polyurea, and the amide and imide nitrogens of biuret type structures. Different trends in the relative intensities of these resonances are observed as a function of the press variables. Significant amounts of urethane formation are not detected; however, low amounts could be obscured by signal overlap. Relaxation studies using variable contact time experiments were complicated by excessively long cross-polarization rates for nonprotonated nitrogens. However, experiments using variable spin lock times prior to fixed contact periods indicate that the cured resin in these composites is probably a homogeneous continuum. The utility of ¹⁵N CP/MAS NMR for elucidating fine structural and morphological information from complex isocyanate-cured wood composites is clearly demonstrated."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Characterization of the wood/isocyanate bondline"]}]}],"canonical_facts":{"dc:contributor.department":["Wood Science and Forest Products"],"dc:creator":["Wendler, Steven L."],"dc:date.accessioned":["2014-03-14T21:39:54Z"],"dc:date.available":["2014-03-14T21:39:54Z","2009-07-10"],"dc:date.issued":["1994"],"dc:description.abstract":["Polymeric diphenylmethane diisocyanate, pMDI, is a wood adhesive that provides excellent composite board properties. Much is unknown about the specific mechanism of pMDI/wood adhesion under conditions that are typical of wood gluing operations. The present research describes the use of ¹⁵N cross-polarization, magic-angle spinning (CP/MAS) NMR as a technique for probing the cure chemistry and bondline morphology of pMDI-bonded wood composites. A 99% ¹⁵N-enriched pMDI resin with desirable adhesive properties was synthesized. A series of model cellulose/¹⁵N-pMDI composites, cured as a function of cellulose precure moisture content, were tested prior to solid wood composites in order to test the feasibility of this technique. Solid wood/¹⁵N-pMDI composites were then cured as a function of wood precure moisture content, cure temperature, and cure time. The ¹⁵N CP/MAS NMR spectra clearly show the dominance of the isocyanate/water reaction on the cure chemistry of all composites tested, both cellulose and solid wood. Four prominent resonances are observed in each spectrum: residual isocyanate, polyurea, and the amide and imide nitrogens of biuret type structures. Different trends in the relative intensities of these resonances are observed as a function of the press variables. Significant amounts of urethane formation are not detected; however, low amounts could be obscured by signal overlap. Relaxation studies using variable contact time experiments were complicated by excessively long cross-polarization rates for nonprotonated nitrogens. However, experiments using variable spin lock times prior to fixed contact periods indicate that the cured resin in these composites is probably a homogeneous continuum. The utility of ¹⁵N CP/MAS NMR for elucidating fine structural and morphological information from complex isocyanate-cured wood composites is clearly demonstrated."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-07102009-040325"],"dc:identifier.uri":["http://hdl.handle.net/10919/43617"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Characterization of the wood/isocyanate bondline"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Wood Science and Forest Products"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:43Z"}