{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/42709"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/42709","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Shape Memory Alloy / Glass Composite Seal for Solid Oxide Fuel Cells","abstract":"Widespread use of solid oxide fuel cells is hindered by a lack of long-term durability of seals between metallic and ceramic components caused by thermal expansion mismatch induced cracking. A novel gas seal design incorporating an engineered thermal expansion gradient in a SrO-La₂O₃-A₂O₃-B₂O₃-SiO₂ glass matrix with a TiNiHf shape memory alloy mesh for active stress relief and crack healing is being developed. Coefficient of thermal expansion (CTE) measurements of the seal and fuel cell components shows the possibility for a thermal expansion gradient. Differential scanning calorimetry and microscopy have shown that the TiNiHf alloy has a shape memory transition in the desired range of 200-250ºC. The oxide glass partially crystallizes during thermal cycling which has been observed through X-ray diffraction and dilatometry. The CTE decreases from 9.3Ã 10-6/°C to 6.6Ã 10-6/°C after thermal cycling. Neutron diffraction data from TiNiHf /glass composite samples reveals that the TiNiHf alloy has the ability of absorbing residual stresses from a glass matrix during martensitic phase transition. There is evidence from microscopy that the glass composition is important in determining if reaction will occur with the TiNiHf alloy. The TiNiHf alloy mesh structures can be created using the 3D printing process. This process has been adapted to allow for printing of very thin wire mesh structures of Ni and NiTi powders with a more suitable binder solution. A bi-layer test fixture has been developed which will be useful for assessing leak rate through seal materials.","abstract_html":"Widespread use of solid oxide fuel cells is hindered by a lack of long-term durability of seals between metallic and ceramic components caused by thermal expansion mismatch induced cracking. A novel gas seal design incorporating an engineered thermal expansion gradient in a SrO-La₂O₃-A₂O₃-B₂O₃-SiO₂ glass matrix with a TiNiHf shape memory alloy mesh for active stress relief and crack healing is being developed. Coefficient of thermal expansion (CTE) measurements of the seal and fuel cell components shows the possibility for a thermal expansion gradient. Differential scanning calorimetry and microscopy have shown that the TiNiHf alloy has a shape memory transition in the desired range of 200-250ºC. The oxide glass partially crystallizes during thermal cycling which has been observed through X-ray diffraction and dilatometry. The CTE decreases from 9.3Ã 10-6/°C to 6.6Ã 10-6/°C after thermal cycling. Neutron diffraction data from TiNiHf /glass composite samples reveals that the TiNiHf alloy has the ability of absorbing residual stresses from a glass matrix during martensitic phase transition. There is evidence from microscopy that the glass composition is important in determining if reaction will occur with the TiNiHf alloy. The TiNiHf alloy mesh structures can be created using the 3D printing process. This process has been adapted to allow for printing of very thin wire mesh structures of Ni and NiTi powders with a more suitable binder solution. A bi-layer test fixture has been developed which will be useful for assessing leak rate through seal materials.","abstract_has_math":false,"creators":["Story, Christopher B."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Science and Engineering","degree_department":"Materials Science and Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":["Lu, P. Kathy"],"committee_members":["Pickrell, Gary R.","Reynolds, William T. Jr."],"year":2007,"date_issued":"2007-05-08","date_published":"2007-05-08","updated_at":"2026-07-22T22:18:53Z","subjects":["3D Printing","Rapid Prototyping","TiNiHf","SrO-La2O3-Al2O3-B2O3-SiO2","Shape Memory Alloy","Gas Sealant","Solid Oxide Fuel Cell"],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-05182007-112950"],"render_values":[{"text":"etd-05182007-112950","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/42709","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Lu, P. Kathy"]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Pickrell, Gary R.","Reynolds, William T. Jr."]},{"key":"dc:contributor.department","label":"Department","values":["Materials Science and Engineering"]},{"key":"dc:creator","label":"Author","values":["Story, Christopher B."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:36:20Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:36:20Z","2007-05-24"]},{"key":"dc:date.issued","label":"Date","values":["2007-05-08"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["3D Printing","Rapid Prototyping","TiNiHf","SrO-La2O3-Al2O3-B2O3-SiO2","Shape Memory Alloy","Gas Sealant","Solid Oxide Fuel Cell"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-05182007-112950"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/42709"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Widespread use of solid oxide fuel cells is hindered by a lack of long-term durability of seals between metallic and ceramic components caused by thermal expansion mismatch induced cracking. A novel gas seal design incorporating an engineered thermal expansion gradient in a SrO-La₂O₃-A₂O₃-B₂O₃-SiO₂ glass matrix with a TiNiHf shape memory alloy mesh for active stress relief and crack healing is being developed. Coefficient of thermal expansion (CTE) measurements of the seal and fuel cell components shows the possibility for a thermal expansion gradient. Differential scanning calorimetry and microscopy have shown that the TiNiHf alloy has a shape memory transition in the desired range of 200-250ºC. The oxide glass partially crystallizes during thermal cycling which has been observed through X-ray diffraction and dilatometry. The CTE decreases from 9.3Ã 10-6/°C to 6.6Ã 10-6/°C after thermal cycling. Neutron diffraction data from TiNiHf /glass composite samples reveals that the TiNiHf alloy has the ability of absorbing residual stresses from a glass matrix during martensitic phase transition. There is evidence from microscopy that the glass composition is important in determining if reaction will occur with the TiNiHf alloy. The TiNiHf alloy mesh structures can be created using the 3D printing process. This process has been adapted to allow for printing of very thin wire mesh structures of Ni and NiTi powders with a more suitable binder solution. A bi-layer test fixture has been developed which will be useful for assessing leak rate through seal materials."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:title","label":"Title","values":["Shape Memory Alloy / Glass Composite Seal for Solid Oxide Fuel Cells"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Lu, P. Kathy"],"dc:contributor.committeemember":["Pickrell, Gary R.","Reynolds, William T. Jr."],"dc:contributor.department":["Materials Science and Engineering"],"dc:creator":["Story, Christopher B."],"dc:date.accessioned":["2014-03-14T21:36:20Z"],"dc:date.available":["2014-03-14T21:36:20Z","2007-05-24"],"dc:date.issued":["2007-05-08"],"dc:description.abstract":["Widespread use of solid oxide fuel cells is hindered by a lack of long-term durability of seals between metallic and ceramic components caused by thermal expansion mismatch induced cracking. A novel gas seal design incorporating an engineered thermal expansion gradient in a SrO-La₂O₃-A₂O₃-B₂O₃-SiO₂ glass matrix with a TiNiHf shape memory alloy mesh for active stress relief and crack healing is being developed. Coefficient of thermal expansion (CTE) measurements of the seal and fuel cell components shows the possibility for a thermal expansion gradient. Differential scanning calorimetry and microscopy have shown that the TiNiHf alloy has a shape memory transition in the desired range of 200-250ºC. The oxide glass partially crystallizes during thermal cycling which has been observed through X-ray diffraction and dilatometry. The CTE decreases from 9.3Ã 10-6/°C to 6.6Ã 10-6/°C after thermal cycling. Neutron diffraction data from TiNiHf /glass composite samples reveals that the TiNiHf alloy has the ability of absorbing residual stresses from a glass matrix during martensitic phase transition. There is evidence from microscopy that the glass composition is important in determining if reaction will occur with the TiNiHf alloy. The TiNiHf alloy mesh structures can be created using the 3D printing process. This process has been adapted to allow for printing of very thin wire mesh structures of Ni and NiTi powders with a more suitable binder solution. A bi-layer test fixture has been developed which will be useful for assessing leak rate through seal materials."],"dc:description.degree":["Master of Science"],"dc:identifier.other":["etd-05182007-112950"],"dc:identifier.uri":["http://hdl.handle.net/10919/42709"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["3D Printing","Rapid Prototyping","TiNiHf","SrO-La2O3-Al2O3-B2O3-SiO2","Shape Memory Alloy","Gas Sealant","Solid Oxide Fuel Cell"],"dc:title":["Shape Memory Alloy / Glass Composite Seal for Solid Oxide Fuel Cells"],"dc:type":["Thesis"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:53Z"}