{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/42466"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/42466","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Preparation and characterization of doped lead zirconate titanate Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃ films","abstract":"Undoped and doped Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃, i. e. PZT, ferroelectric thin films were prepared by chemical solution deposition and spin-coating method. The precursors for making the undoped PZT films were derived from lead acetate, zirconium n-propoxide, and titanium iso-propoxide. In addition, lanthanum acetylacetonate, neodymium acetate, and niobium ethoxide were introduced into the precursor solution to accomplish doping of the corresponding elements. Both doped and undoped PZT films were coated onto Pt/Ti/SiO₂/Si, RuO<sub>x</sub> and single-crystal sapphire substrates of various thickness and annealed at a range of temperatures and times. The effects of dopants were studied in terms of the Curie temperature, crystal distortion, transformation temperature, microstructure, optical properties, and electrical properties. In addition to the dopant effect, the effects of substrates were also investigated with regard to crystallization and preferred orientation. The Curie temperature of the doped and undoped PZT films was determined by in-situ hot-stage transmission electron microscope (TEM) and compared with those of bulk ceramics. Lattice distortion and phase transformation were determined by x-ray diffraction (XRD). Microstructure of the films was characterized by using optical microscopy, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Optical properties were characterized by a UV-VIS-NIR scanning spectrophotometer and electrical properties and fatigue testing were measured on a standardized RT66A using a Virtual-Ground circuit. It was observed that the addition of Nd and La dopants tends to enhance perovskite phase formation and improve electrical properties of PZT films. Higher refractive indices in La and Nd-doped PZT films imply that packing densities of PZT films are improved by adding dopants. Furthermore, the lower leakage currents and improved fatigue properties in PZT films were also observed by the addition of Nb dopants.","abstract_html":"Undoped and doped Pb(Zr&lt;sub&gt;x&lt;/sub&gt;Ti&lt;sub&gt;1-x&lt;/sub&gt;)O₃, i. e. PZT, ferroelectric thin films were prepared by chemical solution deposition and spin-coating method. The precursors for making the undoped PZT films were derived from lead acetate, zirconium n-propoxide, and titanium iso-propoxide. In addition, lanthanum acetylacetonate, neodymium acetate, and niobium ethoxide were introduced into the precursor solution to accomplish doping of the corresponding elements. Both doped and undoped PZT films were coated onto Pt/Ti/SiO₂/Si, RuO&lt;sub&gt;x&lt;/sub&gt; and single-crystal sapphire substrates of various thickness and annealed at a range of temperatures and times. The effects of dopants were studied in terms of the Curie temperature, crystal distortion, transformation temperature, microstructure, optical properties, and electrical properties. In addition to the dopant effect, the effects of substrates were also investigated with regard to crystallization and preferred orientation. The Curie temperature of the doped and undoped PZT films was determined by in-situ hot-stage transmission electron microscope (TEM) and compared with those of bulk ceramics. Lattice distortion and phase transformation were determined by x-ray diffraction (XRD). Microstructure of the films was characterized by using optical microscopy, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Optical properties were characterized by a UV-VIS-NIR scanning spectrophotometer and electrical properties and fatigue testing were measured on a standardized RT66A using a Virtual-Ground circuit. It was observed that the addition of Nd and La dopants tends to enhance perovskite phase formation and improve electrical properties of PZT films. Higher refractive indices in La and Nd-doped PZT films imply that packing densities of PZT films are improved by adding dopants. Furthermore, the lower leakage currents and improved fatigue properties in PZT films were also observed by the addition of Nb dopants.","abstract_has_math":false,"creators":["Chang, Jhing-Fang"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Science and Engineering","degree_department":"Materials Science and Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":["Desu, Seshu B."],"committee_members":["Reynolds, William T. Jr.","Cox, David F."],"year":1992,"date_issued":"1992-08-05","date_published":"1992-08-05","updated_at":"2026-07-22T22:18:41Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-05042010-020142"],"render_values":[{"text":"etd-05042010-020142","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/42466","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Desu, Seshu B."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Reynolds, William T. Jr.","Cox, David F."]},{"key":"dc:contributor.department","label":"Department","values":["Materials Science and Engineering"]},{"key":"dc:creator","label":"Author","values":["Chang, Jhing-Fang"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:35:31Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:35:31Z","2010-05-04"]},{"key":"dc:date.issued","label":"Date","values":["1992-08-05"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-05042010-020142"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/42466"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Undoped and doped Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃, i. e. PZT, ferroelectric thin films were prepared by chemical solution deposition and spin-coating method. The precursors for making the undoped PZT films were derived from lead acetate, zirconium n-propoxide, and titanium iso-propoxide. In addition, lanthanum acetylacetonate, neodymium acetate, and niobium ethoxide were introduced into the precursor solution to accomplish doping of the corresponding elements. Both doped and undoped PZT films were coated onto Pt/Ti/SiO₂/Si, RuO<sub>x</sub> and single-crystal sapphire substrates of various thickness and annealed at a range of temperatures and times. The effects of dopants were studied in terms of the Curie temperature, crystal distortion, transformation temperature, microstructure, optical properties, and electrical properties. In addition to the dopant effect, the effects of substrates were also investigated with regard to crystallization and preferred orientation. The Curie temperature of the doped and undoped PZT films was determined by in-situ hot-stage transmission electron microscope (TEM) and compared with those of bulk ceramics. Lattice distortion and phase transformation were determined by x-ray diffraction (XRD). Microstructure of the films was characterized by using optical microscopy, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Optical properties were characterized by a UV-VIS-NIR scanning spectrophotometer and electrical properties and fatigue testing were measured on a standardized RT66A using a Virtual-Ground circuit. It was observed that the addition of Nd and La dopants tends to enhance perovskite phase formation and improve electrical properties of PZT films. Higher refractive indices in La and Nd-doped PZT films imply that packing densities of PZT films are improved by adding dopants. Furthermore, the lower leakage currents and improved fatigue properties in PZT films were also observed by the addition of Nb dopants."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Preparation and characterization of doped lead zirconate titanate Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃ films"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Desu, Seshu B."],"dc:contributor.committeemember":["Reynolds, William T. Jr.","Cox, David F."],"dc:contributor.department":["Materials Science and Engineering"],"dc:creator":["Chang, Jhing-Fang"],"dc:date.accessioned":["2014-03-14T21:35:31Z"],"dc:date.available":["2014-03-14T21:35:31Z","2010-05-04"],"dc:date.issued":["1992-08-05"],"dc:description.abstract":["Undoped and doped Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃, i. e. PZT, ferroelectric thin films were prepared by chemical solution deposition and spin-coating method. The precursors for making the undoped PZT films were derived from lead acetate, zirconium n-propoxide, and titanium iso-propoxide. In addition, lanthanum acetylacetonate, neodymium acetate, and niobium ethoxide were introduced into the precursor solution to accomplish doping of the corresponding elements. Both doped and undoped PZT films were coated onto Pt/Ti/SiO₂/Si, RuO<sub>x</sub> and single-crystal sapphire substrates of various thickness and annealed at a range of temperatures and times. The effects of dopants were studied in terms of the Curie temperature, crystal distortion, transformation temperature, microstructure, optical properties, and electrical properties. In addition to the dopant effect, the effects of substrates were also investigated with regard to crystallization and preferred orientation. The Curie temperature of the doped and undoped PZT films was determined by in-situ hot-stage transmission electron microscope (TEM) and compared with those of bulk ceramics. Lattice distortion and phase transformation were determined by x-ray diffraction (XRD). Microstructure of the films was characterized by using optical microscopy, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Optical properties were characterized by a UV-VIS-NIR scanning spectrophotometer and electrical properties and fatigue testing were measured on a standardized RT66A using a Virtual-Ground circuit. It was observed that the addition of Nd and La dopants tends to enhance perovskite phase formation and improve electrical properties of PZT films. Higher refractive indices in La and Nd-doped PZT films imply that packing densities of PZT films are improved by adding dopants. Furthermore, the lower leakage currents and improved fatigue properties in PZT films were also observed by the addition of Nb dopants."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-05042010-020142"],"dc:identifier.uri":["http://hdl.handle.net/10919/42466"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Preparation and characterization of doped lead zirconate titanate Pb(Zr<sub>x</sub>Ti<sub>1-x</sub>)O₃ films"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:41Z"}