{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/42200"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/42200","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Durability testing of ceramic candle filters in pressurized-fluidized bed combustion environments","abstract":"Ceramic candle filters were subjected to 500 hour high temperature/ high pressure (HTHP) exposure tests to examine their extended durability in simulated coal pressurized-fluidized bed combustion (PFBC) environments. The candle filter materials analyzed included two SiC filters, one with clay binder and one with a minimal amount of clay binder, a cordierite filter, a mullite candle filter and an aluminosilicate refractory concrete filter. Exposure testing conditions included a range of temperature from 700-850°C and a pressure ranging from 1.7-1.8 MPa. The HTHP tests included exposing the ceramic filter materials to steam and steam-alkali environments. The presence of alkali significantly accelerated the deterioration of the filters. The results of the analysis show that significant crushing strength losses were exhibited by the SiC filters after exposure to HTHP alkali-steam conditions at temperatures as low as 700°C. The expansive and destructive cristobalite phase developed in the SiC filters after most of the treatments. The cordierite candle filter showed a decrease in crushing strength associated with grain growth after each high temperature exposure but few other signs of deterioration were detected. The mullite candle filter and the refractory concrete candle filter showed the least amount of change in crushing strength and overall the most candle stability.","abstract_html":"Ceramic candle filters were subjected to 500 hour high temperature/ high pressure (HTHP) exposure tests to examine their extended durability in simulated coal pressurized-fluidized bed combustion (PFBC) environments. The candle filter materials analyzed included two SiC filters, one with clay binder and one with a minimal amount of clay binder, a cordierite filter, a mullite candle filter and an aluminosilicate refractory concrete filter. Exposure testing conditions included a range of temperature from 700-850°C and a pressure ranging from 1.7-1.8 MPa. The HTHP tests included exposing the ceramic filter materials to steam and steam-alkali environments. The presence of alkali significantly accelerated the deterioration of the filters. The results of the analysis show that significant crushing strength losses were exhibited by the SiC filters after exposure to HTHP alkali-steam conditions at temperatures as low as 700°C. The expansive and destructive cristobalite phase developed in the SiC filters after most of the treatments. The cordierite candle filter showed a decrease in crushing strength associated with grain growth after each high temperature exposure but few other signs of deterioration were detected. The mullite candle filter and the refractory concrete candle filter showed the least amount of change in crushing strength and overall the most candle stability.","abstract_has_math":false,"creators":["Valentino, Karen Rose"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Science and Engineering","degree_department":"Materials Science and Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1993,"date_issued":"1993","date_published":"1993","updated_at":"2026-07-22T22:20:23Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04252009-040418"],"render_values":[{"text":"etd-04252009-040418","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/42200","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Materials Science and Engineering"]},{"key":"dc:creator","label":"Author","values":["Valentino, Karen Rose"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:34:22Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:34:22Z","2009-04-25"]},{"key":"dc:date.issued","label":"Date","values":["1993"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04252009-040418"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/42200"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Ceramic candle filters were subjected to 500 hour high temperature/ high pressure (HTHP) exposure tests to examine their extended durability in simulated coal pressurized-fluidized bed combustion (PFBC) environments. The candle filter materials analyzed included two SiC filters, one with clay binder and one with a minimal amount of clay binder, a cordierite filter, a mullite candle filter and an aluminosilicate refractory concrete filter. Exposure testing conditions included a range of temperature from 700-850°C and a pressure ranging from 1.7-1.8 MPa. The HTHP tests included exposing the ceramic filter materials to steam and steam-alkali environments. The presence of alkali significantly accelerated the deterioration of the filters. The results of the analysis show that significant crushing strength losses were exhibited by the SiC filters after exposure to HTHP alkali-steam conditions at temperatures as low as 700°C. The expansive and destructive cristobalite phase developed in the SiC filters after most of the treatments. The cordierite candle filter showed a decrease in crushing strength associated with grain growth after each high temperature exposure but few other signs of deterioration were detected. The mullite candle filter and the refractory concrete candle filter showed the least amount of change in crushing strength and overall the most candle stability."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Durability testing of ceramic candle filters in pressurized-fluidized bed combustion environments"]}]}],"canonical_facts":{"dc:contributor.department":["Materials Science and Engineering"],"dc:creator":["Valentino, Karen Rose"],"dc:date.accessioned":["2014-03-14T21:34:22Z"],"dc:date.available":["2014-03-14T21:34:22Z","2009-04-25"],"dc:date.issued":["1993"],"dc:description.abstract":["Ceramic candle filters were subjected to 500 hour high temperature/ high pressure (HTHP) exposure tests to examine their extended durability in simulated coal pressurized-fluidized bed combustion (PFBC) environments. The candle filter materials analyzed included two SiC filters, one with clay binder and one with a minimal amount of clay binder, a cordierite filter, a mullite candle filter and an aluminosilicate refractory concrete filter. Exposure testing conditions included a range of temperature from 700-850°C and a pressure ranging from 1.7-1.8 MPa. The HTHP tests included exposing the ceramic filter materials to steam and steam-alkali environments. The presence of alkali significantly accelerated the deterioration of the filters. The results of the analysis show that significant crushing strength losses were exhibited by the SiC filters after exposure to HTHP alkali-steam conditions at temperatures as low as 700°C. The expansive and destructive cristobalite phase developed in the SiC filters after most of the treatments. The cordierite candle filter showed a decrease in crushing strength associated with grain growth after each high temperature exposure but few other signs of deterioration were detected. The mullite candle filter and the refractory concrete candle filter showed the least amount of change in crushing strength and overall the most candle stability."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-04252009-040418"],"dc:identifier.uri":["http://hdl.handle.net/10919/42200"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Durability testing of ceramic candle filters in pressurized-fluidized bed combustion environments"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:23Z"}