An experimental investigation of glass breakage in compartment fires

An experimental investigation has been completed which studied the breaking of window glass by fire. The experiments were carried out in a specially designed compartment to achieve two-layer flows characteristic of normal building fires. The experimental data was collected from two test groups: the first for windows with their edges insulated from the fire (edge-protected) and the second for windows uniformly heated by the fire (edge-unprotected). The results of the edge-protected window tests indicated that the glass breakage was caused by a critical temperature difference between the central heated portion of the pane and the glass edge. The experimental work showed the critical value to be approximately 90C. After the material properties of the glass were determined, the theoretical findings of Keski-Rahkonen were used to obtain a value of 70C; the difference attributed to radiative heating. The test results also demonstrated a distinctive loss of integrity by the windows. When breakage occurred, the cracks spread throughout the glass, joined together and caused at least partial collapse of the pane. The results from the edge-unprotected window tests were quite different. There were relatively few cracks developed and almost no propagation across the glass. Consequently, there was no window collapse in any of these cases. The breakage did initiate at a consistent glass temperature value, however, the mechanism for these tests is not known.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Mechanical Engineering

Department dc:contributor.department

Mechanical Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

1990

Author dc:creator

• Skelly, Michael J.

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Dc Identifier Other

etd-04252009-040332

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/42192