{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/42062"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/42062","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Alkali attack on ceramic filters","abstract":"Experiments were performed to determine a suitable binder material for silicon carbide-based ceramic filter. These experiments included exposure of 42% and 60% alumina, aluminosilicates to potassium and sodium containing environments for the purpose of determining the phases that would form and to determine concentration profiles. In addition, thermodynamic calculations were performed to predict the phases that would form when the alkali reacted with the aluminosilicate. The results of the thermodynamic calculations indicated that the alkali compounds will react at temperatures as low as 800°C. The exposure experiments verified this result. The phases that formed during the sodium vapor exposures and confirmed the thermodynamic calculations and were as follows: 1. sodium metasilicate and a solid solution of sodium aluminum silicates and carnegieite and for potassium vapor exposure. 2. potassium disilicate, kaliophilite-nepheline, potassium aluminate, and 5K₂O-5Al₂O₃-8SiO₂. Experiments also revealed that penetration depth by alkali compounds was restricted to a region near the surface of the material when the combination of temperature and sodium concentration alowed a melt to form. The results also indicated that the 42% alumina, aluminosilicate had superior resistance to alkali attack than the 60% alumina, aluminosilicate at temperatures below 1225°C.","abstract_html":"Experiments were performed to determine a suitable binder material for silicon carbide-based ceramic filter. These experiments included exposure of 42% and 60% alumina, aluminosilicates to potassium and sodium containing environments for the purpose of determining the phases that would form and to determine concentration profiles. In addition, thermodynamic calculations were performed to predict the phases that would form when the alkali reacted with the aluminosilicate. The results of the thermodynamic calculations indicated that the alkali compounds will react at temperatures as low as 800°C. The exposure experiments verified this result. The phases that formed during the sodium vapor exposures and confirmed the thermodynamic calculations and were as follows: 1. sodium metasilicate and a solid solution of sodium aluminum silicates and carnegieite and for potassium vapor exposure. 2. potassium disilicate, kaliophilite-nepheline, potassium aluminate, and 5K₂O-5Al₂O₃-8SiO₂. Experiments also revealed that penetration depth by alkali compounds was restricted to a region near the surface of the material when the combination of temperature and sodium concentration alowed a melt to form. The results also indicated that the 42% alumina, aluminosilicate had superior resistance to alkali attack than the 60% alumina, aluminosilicate at temperatures below 1225°C.","abstract_has_math":false,"creators":["Vass, Raymond J."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Engineering","degree_department":"Materials Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1990,"date_issued":"1990","date_published":"1990","updated_at":"2026-07-22T22:20:09Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04142009-040442"],"render_values":[{"text":"etd-04142009-040442","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/42062","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Materials Engineering"]},{"key":"dc:creator","label":"Author","values":["Vass, Raymond J."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:33:42Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:33:42Z","2009-04-14"]},{"key":"dc:date.issued","label":"Date","values":["1990"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04142009-040442"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/42062"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Experiments were performed to determine a suitable binder material for silicon carbide-based ceramic filter. These experiments included exposure of 42% and 60% alumina, aluminosilicates to potassium and sodium containing environments for the purpose of determining the phases that would form and to determine concentration profiles. In addition, thermodynamic calculations were performed to predict the phases that would form when the alkali reacted with the aluminosilicate. The results of the thermodynamic calculations indicated that the alkali compounds will react at temperatures as low as 800°C. The exposure experiments verified this result. The phases that formed during the sodium vapor exposures and confirmed the thermodynamic calculations and were as follows: 1. sodium metasilicate and a solid solution of sodium aluminum silicates and carnegieite and for potassium vapor exposure. 2. potassium disilicate, kaliophilite-nepheline, potassium aluminate, and 5K₂O-5Al₂O₃-8SiO₂. Experiments also revealed that penetration depth by alkali compounds was restricted to a region near the surface of the material when the combination of temperature and sodium concentration alowed a melt to form. The results also indicated that the 42% alumina, aluminosilicate had superior resistance to alkali attack than the 60% alumina, aluminosilicate at temperatures below 1225°C."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Alkali attack on ceramic filters"]}]}],"canonical_facts":{"dc:contributor.department":["Materials Engineering"],"dc:creator":["Vass, Raymond J."],"dc:date.accessioned":["2014-03-14T21:33:42Z"],"dc:date.available":["2014-03-14T21:33:42Z","2009-04-14"],"dc:date.issued":["1990"],"dc:description.abstract":["Experiments were performed to determine a suitable binder material for silicon carbide-based ceramic filter. These experiments included exposure of 42% and 60% alumina, aluminosilicates to potassium and sodium containing environments for the purpose of determining the phases that would form and to determine concentration profiles. In addition, thermodynamic calculations were performed to predict the phases that would form when the alkali reacted with the aluminosilicate. The results of the thermodynamic calculations indicated that the alkali compounds will react at temperatures as low as 800°C. The exposure experiments verified this result. The phases that formed during the sodium vapor exposures and confirmed the thermodynamic calculations and were as follows: 1. sodium metasilicate and a solid solution of sodium aluminum silicates and carnegieite and for potassium vapor exposure. 2. potassium disilicate, kaliophilite-nepheline, potassium aluminate, and 5K₂O-5Al₂O₃-8SiO₂. Experiments also revealed that penetration depth by alkali compounds was restricted to a region near the surface of the material when the combination of temperature and sodium concentration alowed a melt to form. The results also indicated that the 42% alumina, aluminosilicate had superior resistance to alkali attack than the 60% alumina, aluminosilicate at temperatures below 1225°C."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-04142009-040442"],"dc:identifier.uri":["http://hdl.handle.net/10919/42062"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Alkali attack on ceramic filters"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Materials Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:09Z"}