{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/41978"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/41978","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"The effects of thermal cycling on residual stresses in thick- walled stainless steel pipe","abstract":"The effects of thermal cycling on residual stresses are studied in thick-walled 316L stainless steel pipe. A relatively small AT of 280°F is considered. The residual stresses are measured by an x-ray diffraction technique. The initial stress state of the pipe wall shows periodic and random variability in stress from -30 to 20 ksi. The pipe was thermal cycled between a furnace and a quenchant bath. The macro residual stresses became 10 ksi more compressive after the first thermal cycle. Thereafter no significant changes are measured in the macro residual stresses, however, the micro residual stresses continue to increase linearly with the number of cycles.","abstract_html":"The effects of thermal cycling on residual stresses are studied in thick-walled 316L stainless steel pipe. A relatively small AT of 280°F is considered. The residual stresses are measured by an x-ray diffraction technique. The initial stress state of the pipe wall shows periodic and random variability in stress from -30 to 20 ksi. The pipe was thermal cycled between a furnace and a quenchant bath. The macro residual stresses became 10 ksi more compressive after the first thermal cycle. Thereafter no significant changes are measured in the macro residual stresses, however, the micro residual stresses continue to increase linearly with the number of cycles.","abstract_has_math":false,"creators":["Morgan, Nancy Abigail"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Engineering","degree_department":"Materials Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1990,"date_issued":"1990","date_published":"1990","updated_at":"2026-07-22T22:20:40Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04082009-040419"],"render_values":[{"text":"etd-04082009-040419","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/41978","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Materials Engineering"]},{"key":"dc:creator","label":"Author","values":["Morgan, Nancy Abigail"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:33:14Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:33:14Z","2009-04-08"]},{"key":"dc:date.issued","label":"Date","values":["1990"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04082009-040419"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/41978"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["The effects of thermal cycling on residual stresses are studied in thick-walled 316L stainless steel pipe. A relatively small AT of 280°F is considered. The residual stresses are measured by an x-ray diffraction technique. The initial stress state of the pipe wall shows periodic and random variability in stress from -30 to 20 ksi. The pipe was thermal cycled between a furnace and a quenchant bath. The macro residual stresses became 10 ksi more compressive after the first thermal cycle. Thereafter no significant changes are measured in the macro residual stresses, however, the micro residual stresses continue to increase linearly with the number of cycles."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["The effects of thermal cycling on residual stresses in thick- walled stainless steel pipe"]}]}],"canonical_facts":{"dc:contributor.department":["Materials Engineering"],"dc:creator":["Morgan, Nancy Abigail"],"dc:date.accessioned":["2014-03-14T21:33:14Z"],"dc:date.available":["2014-03-14T21:33:14Z","2009-04-08"],"dc:date.issued":["1990"],"dc:description.abstract":["The effects of thermal cycling on residual stresses are studied in thick-walled 316L stainless steel pipe. A relatively small AT of 280°F is considered. The residual stresses are measured by an x-ray diffraction technique. The initial stress state of the pipe wall shows periodic and random variability in stress from -30 to 20 ksi. The pipe was thermal cycled between a furnace and a quenchant bath. The macro residual stresses became 10 ksi more compressive after the first thermal cycle. Thereafter no significant changes are measured in the macro residual stresses, however, the micro residual stresses continue to increase linearly with the number of cycles."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-04082009-040419"],"dc:identifier.uri":["http://hdl.handle.net/10919/41978"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["The effects of thermal cycling on residual stresses in thick- walled stainless steel pipe"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Materials Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:40Z"}