{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/41448"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/41448","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Characterization of high temperature creep in siliconized silicon carbide using ultrasonic techniques","abstract":"Ultrasonic velocity and attenuation were both measured on samples containing various degrees of damage due to high temperature creep. These results were compared with parameters associated with creep damage such as strain and cavity formation, in order to better understand the mechanisms of creep in Si/SiC and to determine if ultrasonics can be used in evaluating the severity of damage. The data indicated that both ultrasonic velocity and attenuation are directly related to creep strain and can be used in evaluating creep damage. Ultrasonic velocity was found to be exponentially related to creep strain. Cavity formation was found not to significantly affect either of the measured ultrasonic properties. The results indicated that Si/SiC behaves as a two phase material in that high frequency ultrasound propagates primarily through the silicon carbide phase and not by the silicon phase.","abstract_html":"Ultrasonic velocity and attenuation were both measured on samples containing various degrees of damage due to high temperature creep. These results were compared with parameters associated with creep damage such as strain and cavity formation, in order to better understand the mechanisms of creep in Si/SiC and to determine if ultrasonics can be used in evaluating the severity of damage. The data indicated that both ultrasonic velocity and attenuation are directly related to creep strain and can be used in evaluating creep damage. Ultrasonic velocity was found to be exponentially related to creep strain. Cavity formation was found not to significantly affect either of the measured ultrasonic properties. The results indicated that Si/SiC behaves as a two phase material in that high frequency ultrasound propagates primarily through the silicon carbide phase and not by the silicon phase.","abstract_has_math":false,"creators":["Buttram, Jonathan D."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Science and Mechanics","degree_department":"Engineering Science and Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Duke, John C. Jr."],"committee_members":["Stinchcomb, Wayne W.","Cramer, Mark S."],"year":1990,"date_issued":"1990-04-04","date_published":"1990-04-04","updated_at":"2026-07-22T22:19:41Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-03122009-040453"],"render_values":[{"text":"etd-03122009-040453","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/41448","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Duke, John C. Jr."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Stinchcomb, Wayne W.","Cramer, Mark S."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Science and Mechanics"]},{"key":"dc:creator","label":"Author","values":["Buttram, Jonathan D."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:31:04Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:31:04Z","2009-03-12"]},{"key":"dc:date.issued","label":"Date","values":["1990-04-04"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Science and Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-03122009-040453"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/41448"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Ultrasonic velocity and attenuation were both measured on samples containing various degrees of damage due to high temperature creep. These results were compared with parameters associated with creep damage such as strain and cavity formation, in order to better understand the mechanisms of creep in Si/SiC and to determine if ultrasonics can be used in evaluating the severity of damage. The data indicated that both ultrasonic velocity and attenuation are directly related to creep strain and can be used in evaluating creep damage. Ultrasonic velocity was found to be exponentially related to creep strain. Cavity formation was found not to significantly affect either of the measured ultrasonic properties. The results indicated that Si/SiC behaves as a two phase material in that high frequency ultrasound propagates primarily through the silicon carbide phase and not by the silicon phase."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Characterization of high temperature creep in siliconized silicon carbide using ultrasonic techniques"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Duke, John C. Jr."],"dc:contributor.committeemember":["Stinchcomb, Wayne W.","Cramer, Mark S."],"dc:contributor.department":["Engineering Science and Mechanics"],"dc:creator":["Buttram, Jonathan D."],"dc:date.accessioned":["2014-03-14T21:31:04Z"],"dc:date.available":["2014-03-14T21:31:04Z","2009-03-12"],"dc:date.issued":["1990-04-04"],"dc:description.abstract":["Ultrasonic velocity and attenuation were both measured on samples containing various degrees of damage due to high temperature creep. These results were compared with parameters associated with creep damage such as strain and cavity formation, in order to better understand the mechanisms of creep in Si/SiC and to determine if ultrasonics can be used in evaluating the severity of damage. The data indicated that both ultrasonic velocity and attenuation are directly related to creep strain and can be used in evaluating creep damage. Ultrasonic velocity was found to be exponentially related to creep strain. Cavity formation was found not to significantly affect either of the measured ultrasonic properties. The results indicated that Si/SiC behaves as a two phase material in that high frequency ultrasound propagates primarily through the silicon carbide phase and not by the silicon phase."],"dc:description.degree":["Master of Science"],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-03122009-040453"],"dc:identifier.uri":["http://hdl.handle.net/10919/41448"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Characterization of high temperature creep in siliconized silicon carbide using ultrasonic techniques"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Science and Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:19:41Z"}