Structural Performance of Fiber-Reinforced and Welded Wire Fabric-Reinforced Concrete Composite Slabs

The purpose of this research is to evaluate and compare the structural performance of composite floor slabs reinforced with 6 x 6 W1.4/W1.4 welded wire fabric (WWF) and STRUX 90/40 synthetic macro fibers. Slabs were subjected to flexural strength tests and concentrated load tests while monitoring load, steel deck strains, and deflections. Test results obtained from this test program were also compared to results from a similar test program conducted in 2001. Tests were also performed to obtain the average residual-strength of the fiber-reinforced concrete using the ASTM C 1399 (2003) standard test. All slabs were loaded until a complete failure was observed. The observed failure loads were compared to failure loads calculated by design guides published by the American Society of Civil Engineers (ASCE) and the Steel Deck Institute (SDI). The flexural strength tests showed that composite slabs reinforced with synthetic macro fibers and WWF exhibited strength and behavior that was almost identical. The observed values of strength were also within the range that was predicted by ASCE prediction models. At a typical office design load of 70 psf, all slabs exhibited midspan deflections that were much smaller than those necessary for serviceability requirements. The concentrated load tests also showed that the observed strength of all composite slabs tested was above those values predicted by ASCE and SDI models. However, an effective comparison between the WWF-reinforced and synthetic macro fiber-reinforced slab was difficult due to a poor shear bond in the latter slab prior to testing. The results of the ASTM C 1399 test verified the ability of concrete reinforced with synthetic macro fibers to meet average residual-strength values recommended by the SDI.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Civil Engineering

Department dc:contributor.department

Civil Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2006

Author dc:creator

• Ordija, James Louis

Chair dc:contributor.committeechair

• Easterling, William Samuel

Committee members dc:contributor.committeemember

• Murray, Thomas M.
• Roberts-Wollmann, Carin L.

• residual strength
• welded wire fabric
• secondary reinforcement
• composite slabs
• synthetic fibers

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

etd-01092007-000202

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/40539