{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/39573"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/39573","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Characterization of damage mechanisms and behavior in two-dimensionally braided composites subjected to static and fatigue loading","abstract":"In the present research project, four braided composite architectures consisting of graphite fibers in an epoxy matrix were tested under static and fatigue loading conditions to determine damage mechanism types and progressions. The braided architectures consisted of straight axial fiber bundles, which were surrounded by braider fiber bundles oriented at ±a 0 with respect to the axial fiber bundles. Static tension and compression testing was completed first to determine material strengths and basic damage modes for each of the architectures. Under static tension loading, cracking in the braider fiber bundles occurred first, and was followed by splitting in curved regions of the axial fiber bundles. Matrix cracking and kink band formation were found to occur under static compression loading.","abstract_html":"In the present research project, four braided composite architectures consisting of graphite fibers in an epoxy matrix were tested under static and fatigue loading conditions to determine damage mechanism types and progressions. The braided architectures consisted of straight axial fiber bundles, which were surrounded by braider fiber bundles oriented at ±a 0 with respect to the axial fiber bundles. Static tension and compression testing was completed first to determine material strengths and basic damage modes for each of the architectures. Under static tension loading, cracking in the braider fiber bundles occurred first, and was followed by splitting in curved regions of the axial fiber bundles. Matrix cracking and kink band formation were found to occur under static compression loading.","abstract_has_math":false,"creators":["Burr, Scott T."],"institution":"Virginia Tech","degree_name":"Ph. D.","degree_level":"doctoral","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Morris, Don H."],"committee_members":["Johnson, Eric R.","Lesko, John J.","Griffin, Odis Hayden Jr.","Ragab, Saad A."],"year":1996,"date_issued":"1996-05-20","date_published":"1996-05-20","updated_at":"2026-07-22T22:20:23Z","subjects":["textile composites","testing","failure","Fatigue","damage","Modeling"],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-10032007-171922"],"render_values":[{"text":"etd-10032007-171922","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/39573","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Morris, Don H."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Johnson, Eric R.","Lesko, John J.","Griffin, Odis Hayden Jr.","Ragab, Saad A."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Burr, Scott T."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:19:48Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:19:48Z","2007-10-03"]},{"key":"dc:date.issued","label":"Date","values":["1996-05-20"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph. D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["textile composites","testing","failure","Fatigue","damage","Modeling"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-10032007-171922"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/39573"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["In the present research project, four braided composite architectures consisting of graphite fibers in an epoxy matrix were tested under static and fatigue loading conditions to determine damage mechanism types and progressions. The braided architectures consisted of straight axial fiber bundles, which were surrounded by braider fiber bundles oriented at ±a 0 with respect to the axial fiber bundles. Static tension and compression testing was completed first to determine material strengths and basic damage modes for each of the architectures. Under static tension loading, cracking in the braider fiber bundles occurred first, and was followed by splitting in curved regions of the axial fiber bundles. Matrix cracking and kink band formation were found to occur under static compression loading."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Ph. D."]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Characterization of damage mechanisms and behavior in two-dimensionally braided composites subjected to static and fatigue loading"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Morris, Don H."],"dc:contributor.committeemember":["Johnson, Eric R.","Lesko, John J.","Griffin, Odis Hayden Jr.","Ragab, Saad A."],"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Burr, Scott T."],"dc:date.accessioned":["2014-03-14T21:19:48Z"],"dc:date.available":["2014-03-14T21:19:48Z","2007-10-03"],"dc:date.issued":["1996-05-20"],"dc:description.abstract":["In the present research project, four braided composite architectures consisting of graphite fibers in an epoxy matrix were tested under static and fatigue loading conditions to determine damage mechanism types and progressions. The braided architectures consisted of straight axial fiber bundles, which were surrounded by braider fiber bundles oriented at ±a 0 with respect to the axial fiber bundles. Static tension and compression testing was completed first to determine material strengths and basic damage modes for each of the architectures. Under static tension loading, cracking in the braider fiber bundles occurred first, and was followed by splitting in curved regions of the axial fiber bundles. Matrix cracking and kink band formation were found to occur under static compression loading."],"dc:description.degree":["Ph. D."],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-10032007-171922"],"dc:identifier.uri":["http://hdl.handle.net/10919/39573"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["textile composites","testing","failure","Fatigue","damage","Modeling"],"dc:title":["Characterization of damage mechanisms and behavior in two-dimensionally braided composites subjected to static and fatigue loading"],"dc:type":["Dissertation"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["doctoral"],"thesis:degree_name":["Ph. D."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:23Z"}