Cellulose-based fibers from liquid crystalline solutions

Solutions of cellulose esters with different concentrations in dimethylacetamide (DMAc) and with different types of substituents were studied in relation to their liquid crystalline (LC) solution behavior. Classical LC behavior was revealed for all solutions. Critical polymer concentration (V_p^c) is highest for cellulose acetate (CA) and lowest for cellulose acetate butyrate (CAB) with highest degree of butyration. This is opposite to the classical model by Flory which predicts an increase in V_p^c with decreasing aspect ratio (L/d). Fibers were spun from isotropic and anisotropic DMAc solutions of cellulose esters by dry jet/wet spinning process. The mechanical properties, orientation, and crystallinity of the fibers increased as spinning progressed from the isotropic to the anisotropic solution state. High butyryl content enhances both overall solubility and the formation of LC solutions at lower concentration, but it results in lower fiber properties. Unmodified cellulose (C) and cellulose hexanoate (CH) also exhibited LC behavior. The V_p^c value for CH was lower than that obtained for CAB with maximum degree of butyration. This indicates that bulky substituents may lower V_p^c values. The formation of high modulus (152 g/d) cellulose fibers from LC solutions is attributed to the air-gap that exists in the dry jet/wet spinning process. Presence of lithium chloride (LiCl) in the LC solutions of CAB exhibited ionic interactions. Mechano-sorptive creep behavior of the fibers spun from these solutions decreases in the presence of residual LiCl salt. Fibers from blends of CAB and of C with lignin (L) were spun from Lc solution. Morphological investigations demonstrate that CAB and L formed intimately mixed blends whereas C and L were partially mixed. The mechanical properties of the fibers with L increased due to good phase mixing of CAB and L molecules in the fiber matrix.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Materials Engineering Science

Department dc:contributor.department

Materials Engineering Science

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

1992

Author dc:creator

• Davé, Vipul

Chair dc:contributor.committeechair

• Glasser, Wolfgang G.

Committee members dc:contributor.committeemember

• Loos, Alfred C.
• McGrath, James E.
• Wilkes, Garth L.
• Marand, Hervé L.

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Dc Identifier Other

etd-08232007-112345

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/39205