{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/38074"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/38074","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Fatigue behavior of ceramic matrix composites at elevated temperatures under cyclic loading","abstract":"To achieve satisfactory levels of strength, fracture toughness, and reliability for man-rated systems such as jet engines, fiber reinforced ceramic matrix composites are needed. An elevated temperature axial testing system is developed to investigate and characterize fatigue behavior of Nicalon fiber reinforced enhanced silicon carbide matrix. composites at 1800 of under fully reversed cyclic loading. Notch effect on quasi-static tensile response is also considered. Quasi-static and fatigue damage mechanisms and failure modes are examined using various specimen geometries, load levels, fatigue ratios, and laminates stacking sequences by employing a number of NDE techniques. Issues such as damage tolerance and durability are addressed by conducting interrupted fatigue tests at various stages of life for different load levels. Results are compared to the predictions of remaining strength and life, obtained using a performance simulation code. Initial results indicate existence of a threshold stress value which limits the use of the material system.","abstract_html":"To achieve satisfactory levels of strength, fracture toughness, and reliability for man-rated systems such as jet engines, fiber reinforced ceramic matrix composites are needed. An elevated temperature axial testing system is developed to investigate and characterize fatigue behavior of Nicalon fiber reinforced enhanced silicon carbide matrix. composites at 1800 of under fully reversed cyclic loading. Notch effect on quasi-static tensile response is also considered. Quasi-static and fatigue damage mechanisms and failure modes are examined using various specimen geometries, load levels, fatigue ratios, and laminates stacking sequences by employing a number of NDE techniques. Issues such as damage tolerance and durability are addressed by conducting interrupted fatigue tests at various stages of life for different load levels. Results are compared to the predictions of remaining strength and life, obtained using a performance simulation code. Initial results indicate existence of a threshold stress value which limits the use of the material system.","abstract_has_math":false,"creators":["Elahi, Mehran"],"institution":"Virginia Tech","degree_name":"Ph. D.","degree_level":"doctoral","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Reifsnider, Kenneth L."],"committee_members":["Duke, John C. Jr.","Mook, Dean T.","Kriz, Ronald D.","Johnson, Eric R."],"year":1996,"date_issued":"1996-12-19","date_published":"1996-12-19","updated_at":"2026-07-22T22:18:50Z","subjects":["life prediction","ceramic matrix composites","Fatigue","elevated temperature","strength prediction","life","remaining strength"],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-06062008-154429"],"render_values":[{"text":"etd-06062008-154429","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/38074","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Reifsnider, Kenneth L."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Duke, John C. Jr.","Mook, Dean T.","Kriz, Ronald D.","Johnson, Eric R."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Elahi, Mehran"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:12:31Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:12:31Z","2008-06-06"]},{"key":"dc:date.issued","label":"Date","values":["1996-12-19"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph. D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["life prediction","ceramic matrix composites","Fatigue","elevated temperature","strength prediction","life","remaining strength"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-06062008-154429"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/38074"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["To achieve satisfactory levels of strength, fracture toughness, and reliability for man-rated systems such as jet engines, fiber reinforced ceramic matrix composites are needed. An elevated temperature axial testing system is developed to investigate and characterize fatigue behavior of Nicalon fiber reinforced enhanced silicon carbide matrix. composites at 1800 of under fully reversed cyclic loading. Notch effect on quasi-static tensile response is also considered. Quasi-static and fatigue damage mechanisms and failure modes are examined using various specimen geometries, load levels, fatigue ratios, and laminates stacking sequences by employing a number of NDE techniques. Issues such as damage tolerance and durability are addressed by conducting interrupted fatigue tests at various stages of life for different load levels. Results are compared to the predictions of remaining strength and life, obtained using a performance simulation code. Initial results indicate existence of a threshold stress value which limits the use of the material system."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Ph. D."]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Fatigue behavior of ceramic matrix composites at elevated temperatures under cyclic loading"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Reifsnider, Kenneth L."],"dc:contributor.committeemember":["Duke, John C. Jr.","Mook, Dean T.","Kriz, Ronald D.","Johnson, Eric R."],"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Elahi, Mehran"],"dc:date.accessioned":["2014-03-14T21:12:31Z"],"dc:date.available":["2014-03-14T21:12:31Z","2008-06-06"],"dc:date.issued":["1996-12-19"],"dc:description.abstract":["To achieve satisfactory levels of strength, fracture toughness, and reliability for man-rated systems such as jet engines, fiber reinforced ceramic matrix composites are needed. An elevated temperature axial testing system is developed to investigate and characterize fatigue behavior of Nicalon fiber reinforced enhanced silicon carbide matrix. composites at 1800 of under fully reversed cyclic loading. Notch effect on quasi-static tensile response is also considered. Quasi-static and fatigue damage mechanisms and failure modes are examined using various specimen geometries, load levels, fatigue ratios, and laminates stacking sequences by employing a number of NDE techniques. Issues such as damage tolerance and durability are addressed by conducting interrupted fatigue tests at various stages of life for different load levels. Results are compared to the predictions of remaining strength and life, obtained using a performance simulation code. Initial results indicate existence of a threshold stress value which limits the use of the material system."],"dc:description.degree":["Ph. D."],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-06062008-154429"],"dc:identifier.uri":["http://hdl.handle.net/10919/38074"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["life prediction","ceramic matrix composites","Fatigue","elevated temperature","strength prediction","life","remaining strength"],"dc:title":["Fatigue behavior of ceramic matrix composites at elevated temperatures under cyclic loading"],"dc:type":["Dissertation"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["doctoral"],"thesis:degree_name":["Ph. D."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:50Z"}