{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/37334"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/37334","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"A prediction of polymer wear using polymer mechanical properties and surface characterization parameters","abstract":"Polymers were slid on rough hard steel surfaces with normal loads which caused full penetration (real and apparent areas equal) and partial penetration (real less than apparent area). Wear data for polyvinylchloride (PVC) and polychlorotrifluoroethylene (PCTFE) was obtained on a pin-on-disk machine using neutron activation analysis A (NAA). Observations of the wear process were made in the scanning electron microscope (SEM) both before, during, and after the wear experiment. It was observed that these polymers along with Nylon 6-6 tend to wear in discrete sites rather than continuous films. At these discrete sites the polymer shears at an angle which is dependent on the mechanical properties of the polymer and on the asperity angle. There appears to be a minimum shear angle beyond which no wear occurs.","abstract_html":"Polymers were slid on rough hard steel surfaces with normal loads which caused full penetration (real and apparent areas equal) and partial penetration (real less than apparent area). Wear data for polyvinylchloride (PVC) and polychlorotrifluoroethylene (PCTFE) was obtained on a pin-on-disk machine using neutron activation analysis A (NAA). Observations of the wear process were made in the scanning electron microscope (SEM) both before, during, and after the wear experiment. It was observed that these polymers along with Nylon 6-6 tend to wear in discrete sites rather than continuous films. At these discrete sites the polymer shears at an angle which is dependent on the mechanical properties of the polymer and on the asperity angle. There appears to be a minimum shear angle beyond which no wear occurs.","abstract_has_math":false,"creators":["Warren, Jeffery Howard"],"institution":"Virginia Tech","degree_name":"Ph. D.","degree_level":"doctoral","degree_discipline":"Mechanical Engineering","degree_department":"Mechanical Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":["Eiss, Norman S. Jr."],"committee_members":["Mabie, Hamilton H.","Furr, A. Keith","Smith, Charles W."],"year":1976,"date_issued":"1976-08-15","date_published":"1976-08-15","updated_at":"2026-07-22T22:20:11Z","subjects":["polymer wear"],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-02072013-040013"],"render_values":[{"text":"etd-02072013-040013","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/37334","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Eiss, Norman S. Jr."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Mabie, Hamilton H.","Furr, A. Keith","Smith, Charles W."]},{"key":"dc:contributor.department","label":"Department","values":["Mechanical Engineering"]},{"key":"dc:creator","label":"Author","values":["Warren, Jeffery Howard"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T21:09:25Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T21:09:25Z","2013-02-07"]},{"key":"dc:date.issued","label":"Date","values":["1976-08-15"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Mechanical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph. D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["polymer wear"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-02072013-040013"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/37334"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Polymers were slid on rough hard steel surfaces with normal loads which caused full penetration (real and apparent areas equal) and partial penetration (real less than apparent area). Wear data for polyvinylchloride (PVC) and polychlorotrifluoroethylene (PCTFE) was obtained on a pin-on-disk machine using neutron activation analysis A (NAA). Observations of the wear process were made in the scanning electron microscope (SEM) both before, during, and after the wear experiment. It was observed that these polymers along with Nylon 6-6 tend to wear in discrete sites rather than continuous films. At these discrete sites the polymer shears at an angle which is dependent on the mechanical properties of the polymer and on the asperity angle. There appears to be a minimum shear angle beyond which no wear occurs."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Ph. D."]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["BTD"]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["A prediction of polymer wear using polymer mechanical properties and surface characterization parameters"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Eiss, Norman S. Jr."],"dc:contributor.committeemember":["Mabie, Hamilton H.","Furr, A. Keith","Smith, Charles W."],"dc:contributor.department":["Mechanical Engineering"],"dc:creator":["Warren, Jeffery Howard"],"dc:date.accessioned":["2014-03-14T21:09:25Z"],"dc:date.available":["2014-03-14T21:09:25Z","2013-02-07"],"dc:date.issued":["1976-08-15"],"dc:description.abstract":["Polymers were slid on rough hard steel surfaces with normal loads which caused full penetration (real and apparent areas equal) and partial penetration (real less than apparent area). Wear data for polyvinylchloride (PVC) and polychlorotrifluoroethylene (PCTFE) was obtained on a pin-on-disk machine using neutron activation analysis A (NAA). Observations of the wear process were made in the scanning electron microscope (SEM) both before, during, and after the wear experiment. It was observed that these polymers along with Nylon 6-6 tend to wear in discrete sites rather than continuous films. At these discrete sites the polymer shears at an angle which is dependent on the mechanical properties of the polymer and on the asperity angle. There appears to be a minimum shear angle beyond which no wear occurs."],"dc:description.degree":["Ph. D."],"dc:format.medium":["BTD"],"dc:format.mimetype":["application/pdf"],"dc:identifier.other":["etd-02072013-040013"],"dc:identifier.uri":["http://hdl.handle.net/10919/37334"],"dc:language.iso":["en"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["polymer wear"],"dc:title":["A prediction of polymer wear using polymer mechanical properties and surface characterization parameters"],"dc:type":["Dissertation"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Mechanical Engineering"],"thesis:degree_level":["doctoral"],"thesis:degree_name":["Ph. D."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:11Z"}