{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/31918"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/31918","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Characterization of the Interfacial Fracture of Solvated Semi-Interpenetrating Polymer Network (S-IPN) Silicone Hydrogels with a Cyclo-Olefin Polymer (COP)","abstract":"As hydrogel products are manufactured and used for applications ranging from biomedical to agricultural, it is useful to characterize their behavior and interaction with other materials. This thesis investigates the adhesion between two different solvated semi-interpenetrating polymer network (S-IPN) silicone hydrogels and a cyclo-olefin (COP) polymer through experimental, analytical, and numerical methods. Interfacial fracture data was collected through the application of the wedge test, a relatively simple test allowing for the measurement of fracture properties over time in environments of interest. In this case, the test was performed at discrete temperatures within range of 4Ë C to 80Ë C. Two COP adherends were bonded together by a layer of one of the S-IPN silicone hydrogels. Upon the insertion of a wedge between the two adherends, debonding at one of the two interfaces would initiate and propagate at a decreasing rate. Measurements were taken of the debond length over time and applied to develop crack propagation rate versus strain energy release rate (SERR) curves. The SERR values were determined through the application of an analytical model derived for the wedge test geometry and to take into account the effects of the hydrogel interlayer. The time-temperature superposition principle (TTSP) was applied to the crack propagation rate versus SERR curves by shifting the crack propagation rates with the Williams-Landel-Ferry (WLF) equation-based shift factors developed for the bulk behavior of each hydrogel. The application of TTSP broadened the SERR and crack propagation rate ranges and presented a large dependency of the adhesion of the system on the viscoelastic nature of the hydrogels. Power-law fits were applied to the master curves in order to determine parameters that could describe the adhesion of the system and be applied in the development of a finite element model representing the interfacial fracture that occurs for each system. The finite element models were used to validate the analytical model and represent the adhesion of the system such that it could be applied to future geometries of interest in which the S-IPN silicone hydrogels are adhered to the COP substrate. <i>[Files modified per J. Austin, July 9, 2013 Gmc]</i>","abstract_html":"As hydrogel products are manufactured and used for applications ranging from biomedical to agricultural, it is useful to characterize their behavior and interaction with other materials. This thesis investigates the adhesion between two different solvated semi-interpenetrating polymer network (S-IPN) silicone hydrogels and a cyclo-olefin (COP) polymer through experimental, analytical, and numerical methods. Interfacial fracture data was collected through the application of the wedge test, a relatively simple test allowing for the measurement of fracture properties over time in environments of interest. In this case, the test was performed at discrete temperatures within range of 4Ë C to 80Ë C. Two COP adherends were bonded together by a layer of one of the S-IPN silicone hydrogels. Upon the insertion of a wedge between the two adherends, debonding at one of the two interfaces would initiate and propagate at a decreasing rate. Measurements were taken of the debond length over time and applied to develop crack propagation rate versus strain energy release rate (SERR) curves. The SERR values were determined through the application of an analytical model derived for the wedge test geometry and to take into account the effects of the hydrogel interlayer. The time-temperature superposition principle (TTSP) was applied to the crack propagation rate versus SERR curves by shifting the crack propagation rates with the Williams-Landel-Ferry (WLF) equation-based shift factors developed for the bulk behavior of each hydrogel. The application of TTSP broadened the SERR and crack propagation rate ranges and presented a large dependency of the adhesion of the system on the viscoelastic nature of the hydrogels. Power-law fits were applied to the master curves in order to determine parameters that could describe the adhesion of the system and be applied in the development of a finite element model representing the interfacial fracture that occurs for each system. The finite element models were used to validate the analytical model and represent the adhesion of the system such that it could be applied to future geometries of interest in which the S-IPN silicone hydrogels are adhered to the COP substrate. &lt;i&gt;[Files modified per J. Austin, July 9, 2013 Gmc]&lt;/i&gt;","abstract_has_math":false,"creators":["Murray, Katie Virginia"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Science and Mechanics","degree_department":"Engineering Science and Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Dillard, David A."],"committee_members":["Lesko, John J.","Case, Scott W."],"year":2011,"date_issued":"2011-02-02","date_published":"2011-02-02","updated_at":"2026-07-22T22:20:29Z","subjects":["S-IPN hydrogels","confinement","Finite element method","debonding","strain energy release rate","bridging","cyclo-olefin polymers","interfacial fracture"],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04252011-173328"],"render_values":[{"text":"etd-04252011-173328","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/31918","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Dillard, David A."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Lesko, John J.","Case, Scott W."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Science and Mechanics"]},{"key":"dc:creator","label":"Author","values":["Murray, Katie Virginia"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T20:34:18Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T20:34:18Z","2013-07-09"]},{"key":"dc:date.issued","label":"Date","values":["2011-02-02"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Science and Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["S-IPN hydrogels","confinement","Finite element method","debonding","strain energy release rate","bridging","cyclo-olefin polymers","interfacial fracture"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-04252011-173328"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/31918"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["As hydrogel products are manufactured and used for applications ranging from biomedical to agricultural, it is useful to characterize their behavior and interaction with other materials. This thesis investigates the adhesion between two different solvated semi-interpenetrating polymer network (S-IPN) silicone hydrogels and a cyclo-olefin (COP) polymer through experimental, analytical, and numerical methods. Interfacial fracture data was collected through the application of the wedge test, a relatively simple test allowing for the measurement of fracture properties over time in environments of interest. In this case, the test was performed at discrete temperatures within range of 4Ë C to 80Ë C. Two COP adherends were bonded together by a layer of one of the S-IPN silicone hydrogels. Upon the insertion of a wedge between the two adherends, debonding at one of the two interfaces would initiate and propagate at a decreasing rate. Measurements were taken of the debond length over time and applied to develop crack propagation rate versus strain energy release rate (SERR) curves. The SERR values were determined through the application of an analytical model derived for the wedge test geometry and to take into account the effects of the hydrogel interlayer. The time-temperature superposition principle (TTSP) was applied to the crack propagation rate versus SERR curves by shifting the crack propagation rates with the Williams-Landel-Ferry (WLF) equation-based shift factors developed for the bulk behavior of each hydrogel. The application of TTSP broadened the SERR and crack propagation rate ranges and presented a large dependency of the adhesion of the system on the viscoelastic nature of the hydrogels. Power-law fits were applied to the master curves in order to determine parameters that could describe the adhesion of the system and be applied in the development of a finite element model representing the interfacial fracture that occurs for each system. The finite element models were used to validate the analytical model and represent the adhesion of the system such that it could be applied to future geometries of interest in which the S-IPN silicone hydrogels are adhered to the COP substrate. <i>[Files modified per J. Austin, July 9, 2013 Gmc]</i>"]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:title","label":"Title","values":["Characterization of the Interfacial Fracture of Solvated Semi-Interpenetrating Polymer Network (S-IPN) Silicone Hydrogels with a Cyclo-Olefin Polymer (COP)"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Dillard, David A."],"dc:contributor.committeemember":["Lesko, John J.","Case, Scott W."],"dc:contributor.department":["Engineering Science and Mechanics"],"dc:creator":["Murray, Katie Virginia"],"dc:date.accessioned":["2014-03-14T20:34:18Z"],"dc:date.available":["2014-03-14T20:34:18Z","2013-07-09"],"dc:date.issued":["2011-02-02"],"dc:description.abstract":["As hydrogel products are manufactured and used for applications ranging from biomedical to agricultural, it is useful to characterize their behavior and interaction with other materials. This thesis investigates the adhesion between two different solvated semi-interpenetrating polymer network (S-IPN) silicone hydrogels and a cyclo-olefin (COP) polymer through experimental, analytical, and numerical methods. Interfacial fracture data was collected through the application of the wedge test, a relatively simple test allowing for the measurement of fracture properties over time in environments of interest. In this case, the test was performed at discrete temperatures within range of 4Ë C to 80Ë C. Two COP adherends were bonded together by a layer of one of the S-IPN silicone hydrogels. Upon the insertion of a wedge between the two adherends, debonding at one of the two interfaces would initiate and propagate at a decreasing rate. Measurements were taken of the debond length over time and applied to develop crack propagation rate versus strain energy release rate (SERR) curves. The SERR values were determined through the application of an analytical model derived for the wedge test geometry and to take into account the effects of the hydrogel interlayer. The time-temperature superposition principle (TTSP) was applied to the crack propagation rate versus SERR curves by shifting the crack propagation rates with the Williams-Landel-Ferry (WLF) equation-based shift factors developed for the bulk behavior of each hydrogel. The application of TTSP broadened the SERR and crack propagation rate ranges and presented a large dependency of the adhesion of the system on the viscoelastic nature of the hydrogels. Power-law fits were applied to the master curves in order to determine parameters that could describe the adhesion of the system and be applied in the development of a finite element model representing the interfacial fracture that occurs for each system. The finite element models were used to validate the analytical model and represent the adhesion of the system such that it could be applied to future geometries of interest in which the S-IPN silicone hydrogels are adhered to the COP substrate. <i>[Files modified per J. Austin, July 9, 2013 Gmc]</i>"],"dc:description.degree":["Master of Science"],"dc:identifier.other":["etd-04252011-173328"],"dc:identifier.uri":["http://hdl.handle.net/10919/31918"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["S-IPN hydrogels","confinement","Finite element method","debonding","strain energy release rate","bridging","cyclo-olefin polymers","interfacial fracture"],"dc:title":["Characterization of the Interfacial Fracture of Solvated Semi-Interpenetrating Polymer Network (S-IPN) Silicone Hydrogels with a Cyclo-Olefin Polymer (COP)"],"dc:type":["Thesis"],"thesis:degree_discipline":["Engineering Science and Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:29Z"}