{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/31522"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/31522","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Mechanically Processed Alumina Reinforced Ultra-high Molecular Weight Polyethylene (UHMWPE) Matrix Composites","abstract":"Alumina particles filled Ultra-high Molecular Weight Polyethylene (UHMWPE), with Al2O3 contents 0, 1, and 2.5 wt% were milled for up to 10 hours by the mechanical alloying (MA) process performed at room temperature to produce composite powders. Compression molding was utilized to produce sheets out of the milled powders. A partial phase transformation from orthorhombic and amorphous phases to monoclinic phase was observed to occur for both the un-reinforced and reinforced UHMWPE in the solid state, which disappeared after using compression molding to produce composite sheets. The volume fraction of the monoclinic phase increased with milling time, mostly at the expense of the amorphous phase. The melting temperature decreased as a function of milling time as a result of modifications in the UHMWPE molecular structure caused by the milling. At the same time, for a given alumina composition the activation energy of melting increased with milling time. Generally, the crystallinity of the molded sheets increased with milling time, and this caused the yield strength and elastic modulus to increase with milling time for a given alumina composition. However, the tensile strength and ductility remained about the same.","abstract_html":"Alumina particles filled Ultra-high Molecular Weight Polyethylene (UHMWPE), with Al2O3 contents 0, 1, and 2.5 wt% were milled for up to 10 hours by the mechanical alloying (MA) process performed at room temperature to produce composite powders. Compression molding was utilized to produce sheets out of the milled powders. A partial phase transformation from orthorhombic and amorphous phases to monoclinic phase was observed to occur for both the un-reinforced and reinforced UHMWPE in the solid state, which disappeared after using compression molding to produce composite sheets. The volume fraction of the monoclinic phase increased with milling time, mostly at the expense of the amorphous phase. The melting temperature decreased as a function of milling time as a result of modifications in the UHMWPE molecular structure caused by the milling. At the same time, for a given alumina composition the activation energy of melting increased with milling time. Generally, the crystallinity of the molded sheets increased with milling time, and this caused the yield strength and elastic modulus to increase with milling time for a given alumina composition. However, the tensile strength and ductility remained about the same.","abstract_has_math":false,"creators":["Elmkharram, Hesham Moh. A."],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Materials Science and Engineering","degree_department":"Materials Science and Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2013,"date_issued":"2013-03-08","date_published":"2013-03-08","updated_at":"2026-07-22T22:19:35Z","subjects":["Mechanical Alloying","Polymer Matrix Composites","Particles Reinforcement"],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-03222013-143305"],"render_values":[{"text":"etd-03222013-143305","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/31522","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Materials Science and Engineering"]},{"key":"dc:creator","label":"Author","values":["Elmkharram, Hesham Moh. A."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T20:32:48Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T20:32:48Z","2013-04-02"]},{"key":"dc:date.issued","label":"Date","values":["2013-03-08"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Mechanical Alloying","Polymer Matrix Composites","Particles Reinforcement"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-03222013-143305"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/31522"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Alumina particles filled Ultra-high Molecular Weight Polyethylene (UHMWPE), with Al2O3 contents 0, 1, and 2.5 wt% were milled for up to 10 hours by the mechanical alloying (MA) process performed at room temperature to produce composite powders. Compression molding was utilized to produce sheets out of the milled powders. A partial phase transformation from orthorhombic and amorphous phases to monoclinic phase was observed to occur for both the un-reinforced and reinforced UHMWPE in the solid state, which disappeared after using compression molding to produce composite sheets. The volume fraction of the monoclinic phase increased with milling time, mostly at the expense of the amorphous phase. The melting temperature decreased as a function of milling time as a result of modifications in the UHMWPE molecular structure caused by the milling. At the same time, for a given alumina composition the activation energy of melting increased with milling time. Generally, the crystallinity of the molded sheets increased with milling time, and this caused the yield strength and elastic modulus to increase with milling time for a given alumina composition. However, the tensile strength and ductility remained about the same."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:title","label":"Title","values":["Mechanically Processed Alumina Reinforced Ultra-high Molecular Weight Polyethylene (UHMWPE) Matrix Composites"]}]}],"canonical_facts":{"dc:contributor.department":["Materials Science and Engineering"],"dc:creator":["Elmkharram, Hesham Moh. A."],"dc:date.accessioned":["2014-03-14T20:32:48Z"],"dc:date.available":["2014-03-14T20:32:48Z","2013-04-02"],"dc:date.issued":["2013-03-08"],"dc:description.abstract":["Alumina particles filled Ultra-high Molecular Weight Polyethylene (UHMWPE), with Al2O3 contents 0, 1, and 2.5 wt% were milled for up to 10 hours by the mechanical alloying (MA) process performed at room temperature to produce composite powders. Compression molding was utilized to produce sheets out of the milled powders. A partial phase transformation from orthorhombic and amorphous phases to monoclinic phase was observed to occur for both the un-reinforced and reinforced UHMWPE in the solid state, which disappeared after using compression molding to produce composite sheets. The volume fraction of the monoclinic phase increased with milling time, mostly at the expense of the amorphous phase. The melting temperature decreased as a function of milling time as a result of modifications in the UHMWPE molecular structure caused by the milling. At the same time, for a given alumina composition the activation energy of melting increased with milling time. Generally, the crystallinity of the molded sheets increased with milling time, and this caused the yield strength and elastic modulus to increase with milling time for a given alumina composition. However, the tensile strength and ductility remained about the same."],"dc:description.degree":["Master of Science"],"dc:identifier.other":["etd-03222013-143305"],"dc:identifier.uri":["http://hdl.handle.net/10919/31522"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["Mechanical Alloying","Polymer Matrix Composites","Particles Reinforcement"],"dc:title":["Mechanically Processed Alumina Reinforced Ultra-high Molecular Weight Polyethylene (UHMWPE) Matrix Composites"],"dc:type":["Thesis"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:19:35Z"}