{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/31093"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/31093","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Quasi-Static and Fatigue Evaluation of Pultruded Vinyl Ester/E-Glass Composites","abstract":"The quasi-static strength, stiffness, and fatigue properties of cross-ply, angle-ply, and quasi-isotropic vinyl ester/E-glass non-woven tricot stitched fabric composite laminates fabricated from the Continuous Resin Transfer Molding (CRTM) pultrusion process were the focus of this research. The tricot stitch and the 6% vinyl ester matrix cure shrinkage were found to play key roles in the quasi-static and fatigue strength and stiffness properties of these laminates. Laminates tested transverse to the pultrusion axis had greater fiber undulation and maximum of 44% quasi-static strength reduction and 8% stiffness reduction compared with axially tested specimens. While the matrix failure strain was 1.9%, failure strain of these laminates range over 1.91 to 2.08% when tested along the pultrusion axis and as low as 1.29% transverse to the pultrusion axis. Fatigue evaluation, in load control mode, evaluated laminate S-N, stiffness reduction, and residual strength. Measured S-N curves and residual strength curves compared with literature were found most like woven fabric laminates, well below aerospace grade laminates. Residual strength and life analysis using Reifsnider's methodology [43], revealed that the choice of quasi-static strength and stiffness, S-N curve, laminate stiffness reduction, and residual strength shape parameter, J, strongly affect predicted life. Predictions at high fatigue stress/low cycle were more exact than at low stress; the S-N curve was steep initially but at low stress/high cycle was nearly horizontal. The best predictions utilized separate off-axis stiffness reductions of E2 obtained from cross-ply and G12 from angle-ply laminates, the quasi-static strength and stiffness of the laminate predicted, and the average S-N and residual strength curves.","abstract_html":"The quasi-static strength, stiffness, and fatigue properties of cross-ply, angle-ply, and quasi-isotropic vinyl ester/E-glass non-woven tricot stitched fabric composite laminates fabricated from the Continuous Resin Transfer Molding (CRTM) pultrusion process were the focus of this research. The tricot stitch and the 6% vinyl ester matrix cure shrinkage were found to play key roles in the quasi-static and fatigue strength and stiffness properties of these laminates. Laminates tested transverse to the pultrusion axis had greater fiber undulation and maximum of 44% quasi-static strength reduction and 8% stiffness reduction compared with axially tested specimens. While the matrix failure strain was 1.9%, failure strain of these laminates range over 1.91 to 2.08% when tested along the pultrusion axis and as low as 1.29% transverse to the pultrusion axis. Fatigue evaluation, in load control mode, evaluated laminate S-N, stiffness reduction, and residual strength. Measured S-N curves and residual strength curves compared with literature were found most like woven fabric laminates, well below aerospace grade laminates. Residual strength and life analysis using Reifsnider's methodology [43], revealed that the choice of quasi-static strength and stiffness, S-N curve, laminate stiffness reduction, and residual strength shape parameter, J, strongly affect predicted life. Predictions at high fatigue stress/low cycle were more exact than at low stress; the S-N curve was steep initially but at low stress/high cycle was nearly horizontal. The best predictions utilized separate off-axis stiffness reductions of E2 obtained from cross-ply and G12 from angle-ply laminates, the quasi-static strength and stiffness of the laminate predicted, and the average S-N and residual strength curves.","abstract_has_math":false,"creators":["Phifer, Stephan Paul"],"institution":"Virginia Tech","degree_name":"Master of Science","degree_level":"masters","degree_discipline":"Engineering Mechanics","degree_department":"Engineering Mechanics","school":null,"contributors":[],"advisors":[],"committee_chairs":["Lesko, John J."],"committee_members":["Kapania, Rakesh K.","Gao, David Y."],"year":1998,"date_issued":"1998-12-17","date_published":"1998-12-17","updated_at":"2026-07-22T22:20:07Z","subjects":["Fatigue","Composite","Residual Strength","Pultrusion"],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-013199-185939"],"render_values":[{"text":"etd-013199-185939","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/31093","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Lesko, John J."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Kapania, Rakesh K.","Gao, David Y."]},{"key":"dc:contributor.department","label":"Department","values":["Engineering Mechanics"]},{"key":"dc:creator","label":"Author","values":["Phifer, Stephan Paul"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T20:31:14Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T20:31:14Z","1999-02-02"]},{"key":"dc:date.issued","label":"Date","values":["1998-12-17"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Engineering Mechanics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Fatigue","Composite","Residual Strength","Pultrusion"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-013199-185939"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/31093"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["The quasi-static strength, stiffness, and fatigue properties of cross-ply, angle-ply, and quasi-isotropic vinyl ester/E-glass non-woven tricot stitched fabric composite laminates fabricated from the Continuous Resin Transfer Molding (CRTM) pultrusion process were the focus of this research. The tricot stitch and the 6% vinyl ester matrix cure shrinkage were found to play key roles in the quasi-static and fatigue strength and stiffness properties of these laminates. Laminates tested transverse to the pultrusion axis had greater fiber undulation and maximum of 44% quasi-static strength reduction and 8% stiffness reduction compared with axially tested specimens. While the matrix failure strain was 1.9%, failure strain of these laminates range over 1.91 to 2.08% when tested along the pultrusion axis and as low as 1.29% transverse to the pultrusion axis. Fatigue evaluation, in load control mode, evaluated laminate S-N, stiffness reduction, and residual strength. Measured S-N curves and residual strength curves compared with literature were found most like woven fabric laminates, well below aerospace grade laminates. Residual strength and life analysis using Reifsnider's methodology [43], revealed that the choice of quasi-static strength and stiffness, S-N curve, laminate stiffness reduction, and residual strength shape parameter, J, strongly affect predicted life. Predictions at high fatigue stress/low cycle were more exact than at low stress; the S-N curve was steep initially but at low stress/high cycle was nearly horizontal. The best predictions utilized separate off-axis stiffness reductions of E2 obtained from cross-ply and G12 from angle-ply laminates, the quasi-static strength and stiffness of the laminate predicted, and the average S-N and residual strength curves."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Master of Science"]},{"key":"dc:title","label":"Title","values":["Quasi-Static and Fatigue Evaluation of Pultruded Vinyl Ester/E-Glass Composites"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Lesko, John J."],"dc:contributor.committeemember":["Kapania, Rakesh K.","Gao, David Y."],"dc:contributor.department":["Engineering Mechanics"],"dc:creator":["Phifer, Stephan Paul"],"dc:date.accessioned":["2014-03-14T20:31:14Z"],"dc:date.available":["2014-03-14T20:31:14Z","1999-02-02"],"dc:date.issued":["1998-12-17"],"dc:description.abstract":["The quasi-static strength, stiffness, and fatigue properties of cross-ply, angle-ply, and quasi-isotropic vinyl ester/E-glass non-woven tricot stitched fabric composite laminates fabricated from the Continuous Resin Transfer Molding (CRTM) pultrusion process were the focus of this research. The tricot stitch and the 6% vinyl ester matrix cure shrinkage were found to play key roles in the quasi-static and fatigue strength and stiffness properties of these laminates. Laminates tested transverse to the pultrusion axis had greater fiber undulation and maximum of 44% quasi-static strength reduction and 8% stiffness reduction compared with axially tested specimens. While the matrix failure strain was 1.9%, failure strain of these laminates range over 1.91 to 2.08% when tested along the pultrusion axis and as low as 1.29% transverse to the pultrusion axis. Fatigue evaluation, in load control mode, evaluated laminate S-N, stiffness reduction, and residual strength. Measured S-N curves and residual strength curves compared with literature were found most like woven fabric laminates, well below aerospace grade laminates. Residual strength and life analysis using Reifsnider's methodology [43], revealed that the choice of quasi-static strength and stiffness, S-N curve, laminate stiffness reduction, and residual strength shape parameter, J, strongly affect predicted life. Predictions at high fatigue stress/low cycle were more exact than at low stress; the S-N curve was steep initially but at low stress/high cycle was nearly horizontal. The best predictions utilized separate off-axis stiffness reductions of E2 obtained from cross-ply and G12 from angle-ply laminates, the quasi-static strength and stiffness of the laminate predicted, and the average S-N and residual strength curves."],"dc:description.degree":["Master of Science"],"dc:identifier.other":["etd-013199-185939"],"dc:identifier.uri":["http://hdl.handle.net/10919/31093"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["Fatigue","Composite","Residual Strength","Pultrusion"],"dc:title":["Quasi-Static and Fatigue Evaluation of Pultruded Vinyl Ester/E-Glass Composites"],"dc:type":["Thesis"],"thesis:degree_discipline":["Engineering Mechanics"],"thesis:degree_level":["masters"],"thesis:degree_name":["Master of Science"],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:07Z"}